NORYL™ Resin SE1GFN1E

NORYL SE1GFN1E resin is a 10% glass fiber reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V1 at 1.5mm along with UL746C Outdoor Suitability rating of F1 and RTI 110°C. NORYL SE1GFN1E exhibits high heat resistance, good dielectric strength, dimensional stability, hydrolytic stability, and very low moisture absorption. This material is an excellent candidate for appliance internals, indoor and outdoor electrical enclosures / housings / connectors. No PFAS intentionally added to this grade.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Dimensional stability
Flame Retardant
High stiffness/Strength
Hydrolytic Stability
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
Non Cl/Br flame retardant
Non halogenated flame retardant

Industry

Material previously used in

Commercial Appliance
Electrical
Energy Management
Home Appliances
Mobile Phone - Computer - Tablets
Water Management

Applications

Possible usage of material

Building and Construction
Aerospace
Audio
Auto Aftermarket
Auto Electrical
Battery Pack
Building Accessory
Circuit Protection
Cladding/Roof
Coffee Maker/Espresso Machine
Dishwasher
Displays
Document Handling
Electrical
Electronic Components
Enclosure/Housing/Cover
Enclosures
Energy Management
Engine Component
EV/HEV Battery
Eyeglasses
Fixture Bath/Shower
Freezer
Humidity Control
Individual Equipment
Inverter
Medical Device
Meter Gas
Monitoring and Imaging
Personal Computing
Photovoltaic Components
Plumbing
Power Manangement
Pump
Respiratory
Wireless Communications
Wiring Devices
fuse box
connector
junction box
power
energy
solar
pv
micro inverter
alternative energy
electrical component
electronic component
battery protection

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	-	Ω.cm	ASTM D257
Relative Permittivity, 50/60 Hz	-	-	ASTM D150
Relative Permittivity, 1 MHz	-	-	ASTM D150
Dissipation Factor, 50/60 Hz	-	-	ASTM D150
Dissipation Factor, 1 MHz	-	-	ASTM D150
High Voltage Arc Track Rate {PLC}	-	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	-	PLC Code	UL 746A
High Amp Arc Ignition (HAI), PLC 1	-	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 2	-	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 0	-	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 1	-	mm	UL 746A

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	-	-	-
UL Yellow Card Link 2	-	-	-
UL Recognized, 94V-1 Flame Class Rating	-	mm	UL 94
UV-light, water exposure/immersion	-	-	UL 746C
Oxygen Index (LOI)	-	%	ASTM D2863

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	-	J/m	ASTM D256
Izod Impact, notched, -40°C	-	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	-	°C
Drying Time	-	Hrs
Drying Time (Cumulative)	-	Hrs
Maximum Moisture Content	-	%
Melt Temperature	-	°C
Nozzle Temperature	-	°C
Front - Zone 3 Temperature	-	°C
Middle - Zone 2 Temperature	-	°C
Rear - Zone 1 Temperature	-	°C
Mold Temperature	-	°C
Back Pressure	-	MPa
Screw Speed	-	rpm
Shot to Cylinder Size	-	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	-	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	-	%	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	-	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	-	MPa	ASTM D790
Hardness, Rockwell L	-	-	ASTM D785

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	-	-	ASTM D792
Water Absorption, (23°C/24hrs)	-	%	ASTM D570
Water Absorption, (23°C/Saturated)	-	%	ASTM D570
Mold Shrinkage, flow, 3.2 mm	-	%	SABIC method
PFAS	-	-

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	-	°C	ASTM D1525
HDT, 1.82 MPa, 6.4 mm, unannealed	-	°C	ASTM D648
Relative Temp Index, Elec	-	°C	UL 746B
Relative Temp Index, Mech w/impact	-	°C	UL 746B
Relative Temp Index, Mech w/o impact	-	°C	UL 746B

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	-	Ω.cm	ASTM D257
Relative Permittivity, 50/60 Hz	-	-	ASTM D150
Relative Permittivity, 1 MHz	-	-	ASTM D150
Dissipation Factor, 50/60 Hz	-	-	ASTM D150
Dissipation Factor, 1 MHz	-	-	ASTM D150
High Voltage Arc Track Rate {PLC}	-	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	-	PLC Code	UL 746A
High Amp Arc Ignition (HAI), PLC 2	-	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 1	-	mm	UL 746A

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	-	-	-
UL Yellow Card Link 2	-	-	-
UL Recognized, 94-5VA Flame Class Rating	-	mm	UL 94
UL Recognized, 94V-1 Flame Class Rating	-	mm	UL 94
Oxygen Index (LOI)	-	%	ASTM D2863

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	-	J/m	ASTM D256
Izod Impact, notched, -40°C	-	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	-	°C
Drying Time	-	Hrs
Drying Time (Cumulative)	-	Hrs
Maximum Moisture Content	-	%
Melt Temperature	-	°C
Nozzle Temperature	-	°C
Front - Zone 3 Temperature	-	°C
Middle - Zone 2 Temperature	-	°C
Rear - Zone 1 Temperature	-	°C
Mold Temperature	-	°C
Back Pressure	-	MPa
Screw Speed	-	rpm
Shot to Cylinder Size	-	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	-	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	-	%	ASTM D638
Flexural Stress, brk, 1.3 mm/min, 50 mm span	-	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	-	MPa	ASTM D790
Hardness, Rockwell L	-	-	ASTM D785

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	-	-	ASTM D792
Water Absorption, (23°C/24hrs)	-	%	ASTM D570
Water Absorption, (23°C/Saturated)	-	%	ASTM D570
Mold Shrinkage, flow, 3.2 mm	-	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Vicat Softening Temp, Rate B/50	-	°C	ASTM D1525
HDT, 1.82 MPa, 6.4 mm, unannealed	-	°C	ASTM D648
Relative Temp Index, Elec	-	°C	UL 746B
Relative Temp Index, Mech w/impact	-	°C	UL 746B
Relative Temp Index, Mech w/o impact	-	°C	UL 746B

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	1.E+15	Ω.cm	IEC 60093
Surface Resistivity, ROA	>1.E+15	Ω	IEC 60093
Dielectric Strength, in oil, 0.8 mm	33	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 1.6 mm	26	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 3.2 mm	16	kV/mm	IEC 60243-1
Relative Permittivity, 1 MHz	2.7	-	IEC 60250
Dissipation Factor, 50/60 Hz	0.005	-	IEC 60250
Dissipation Factor, 1 MHz	0.003	-	IEC 60250
Comparative Tracking Index	250	V	IEC 60112
Relative Permittivity, 50/60 Hz	2.8	-	IEC 60250
Comparative Tracking Index (UL) {PLC}	2	PLC Code	UL 746A
High Amp Arc Ignition (HAI), PLC 1	≥0.8	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 1	≥0.8	mm	UL 746A
High Voltage Arc Track Rate {PLC}	4	PLC Code	UL 746A

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94-5VA Flame Class Rating	≥2.5	mm	UL 94
UL Recognized, 94V-1 Flame Class Rating	≥0.8	mm	UL 94
Glow Wire Flammability Index, 1.0 mm	960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 1.5 mm	960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 2.0 mm	960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 2.5 mm	960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 3.0 mm	960	°C	IEC 60695-2-12
Needle Flame Test, 10 s , passes at	1.5	mm	IEC 60695-2-2
Glow Wire Ignitability Temperature, 1.0 mm	775	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 1.5 mm	775	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 2.0 mm	800	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 2.5 mm	800	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 3.0 mm	800	°C	IEC 60695-2-13
UV-light, water exposure/immersion	F2	-	UL 746C
Oxygen Index (LOI)	30	%	ISO 4589

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80103 -40°C*	6	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	25	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	25	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	7	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	6	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	6	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80103 sp=62mm*	5	kJ/m²	ISO 179/1eA
*Charpy -40°C, V-notch Edgew 80103 sp=62mm*	5	kJ/m²	ISO 179/1eA
*Charpy -30°C, Unnotch Edgew 80103 sp=62mm*	30	kJ/m²	ISO 179/1eU
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	30	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 120	°C
Drying Time	2 - 3	Hrs
Melt Temperature	280 - 300	°C
Nozzle Temperature	260 - 280	°C
Front - Zone 3 Temperature	280 - 300	°C
Middle - Zone 2 Temperature	260 - 280	°C
Rear - Zone 1 Temperature	240 - 260	°C
Hopper Temperature	60 - 80	°C
Mold Temperature	80 - 120	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Taber Abrasion, CS-17, 1 kg	50	mg/1000cy	SABIC method
Tensile Stress, yield, 5 mm/min	75	MPa	ISO 527
Tensile Stress, break, 5 mm/min	70	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	2.5	%	ISO 527
Tensile Strain, break, 5 mm/min	3	%	ISO 527
Tensile Modulus, 1 mm/min	4000	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	110	MPa	ISO 178
Flexural Modulus, 2 mm/min	3000	MPa	ISO 178
Ball Indentation Hardness, H358/30	100	MPa	ISO 2039-1

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
PFAS	Not Intentionally added	-
Specific Gravity	1.16	-	ASTM D792
Mold Shrinkage on Tensile Bar, flow	0.3 - 0.5	%	SABIC method
Density	1.17	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)	0.22	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.07	%	ISO 62
Melt Volume Rate, MVR at 280°C/10.0 kg	15	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
CTE, -40°C to 40°C, flow	5.5E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	6.8E-05	1/°C	ASTM E831
Thermal Conductivity	0.27	W/m-°C	ISO 8302
CTE, -40°C to 40°C, flow	5.5E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	6.8E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, flow	5.E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	7.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Ball Pressure Test, approximate maximum	135	°C	IEC 60695-10-2
Vicat Softening Temp, Rate A/50	145	°C	ISO 306
Vicat Softening Temp, Rate B/50	140	°C	ISO 306
Vicat Softening Temp, Rate B/120	145	°C	ISO 306
*HDT/Be, 0.45MPa Edgew 120104 sp=100mm*	140	°C	ISO 75/Be
*HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm*	135	°C	ISO 75/Ae
Relative Temp Index, Elec	110	°C	UL 746B
Relative Temp Index, Mech w/impact	105	°C	UL 746B
Relative Temp Index, Mech w/o impact	110	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES

NORYL™ Resin SE1GFN1E

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Related Documents