NORYL SG039916 resin is a 30% glass fiber reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA) with over 35% post-consumer recycled content. This injection moldable grade has high stiffness (flexural modulus 8200 MPa), excellent chemical resistance, and high heat resistance. NORYL SG039916 resin is an excellent candidate for a wide variety of applications including automotive under the bonnet applications and water meter housings.
You can get in touch with us in these regions to buy the material
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index | 225 | V | IEC 60112 |
| Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 2 | 3 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 4 | 2 | mm | UL 746A |
| High Amp Arc Ignition, 1.5 mm | 0 | PLC Code | UL 746A |
| High Amp Arc Ignition, 3.0 mm | 0 | PLC Code | UL 746A |
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
| Oxygen Index (LOI) | 27 | % | ISO 4589 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 8 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 8 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 50 | kJ/m² | ISO 180/1U |
| Charpy Impact, notched, 23°C | 8 | kJ/m² | ISO 179/2C |
| Charpy Impact, notched, -30°C | 8 | kJ/m² | ISO 179/2C |
| Charpy Impact, unnotched, 23°C | 50 | kJ/m² | ISO 179/2C |
| Charpy Impact, unnotched, -30°C | 50 | kJ/m² | ISO 179/2C |
| Izod Impact, notched, 23°C | 125 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 95 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 931 | J/m | ASTM D4812 |
| Izod Impact, unnotched, -30°C | 870 | J/m | ASTM D4812 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2 - 3 | Hrs | |
| Maximum Moisture Content | 0.07 | % | |
| Melt Temperature | 280 - 320 | °C | |
| Nozzle Temperature | 270 - 310 | °C | |
| Front - Zone 3 Temperature | 280 - 320 | °C | |
| Middle - Zone 2 Temperature | 270 - 310 | °C | |
| Rear - Zone 1 Temperature | 260 - 300 | °C | |
| Hopper Temperature | 60 - 80 | °C | |
| Mold Temperature | 100 - 120 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Modulus, 1 mm/min | 7800 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 120 | MPa | ISO 527 |
| Tensile Nominal Strain, break, 5 mm/min | 2.5 | % | ISO 527 |
| Flexural Modulus, 2 mm/min | 6500 | MPa | ISO 178 |
| Flexural Stress, break, 2 mm/min | 190 | MPa | ISO 178 |
| Tensile Modulus, 5 mm/min | 8952 | MPa | ASTM D638 |
| Tensile Stress, yld, Type I, 5 mm/min | 145 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 144 | MPa | ASTM D638 |
| Tensile Nominal Strain, brk, Type I, 5 mm/min | 2.9 | % | ASTM D638 |
| Flexural Modulus | 8510 | MPa | ASTM D790 |
| Flexural Stress | 227 | MPa | ASTM D790 |
| Ball Indentation Hardness, H358/30 | 213 | MPa | ISO 2039-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Moisture Absorption, (23°C/50% RH/24hrs) | 0.47 | % | ISO 62-4 |
| Water Absorption, (23°C/saturated) | 2.4 | % | ISO 62-1 |
| Mold Shrinkage, flow | 0.5 | % | SABIC method |
| Mold Shrinkage, xflow | 1.1 | % | SABIC method |
| Melt Volume Rate, MVR at 280°C/5.0 kg | 6 | cm³/10 min | ISO 1133 |
| Specific Gravity | 1.3 | - | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.47 | % | ASTM D570 |
| Water Absorption, (23°C/ saturated) | 2.4 | % | ASTM D570 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 194 | °C | ISO 75/Af |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 210 | °C | ISO 75/Bf |
| HDT, 1.82 MPa, 3.2mm, unannealed | 191 | °C | ASTM D648 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 209 | °C | ASTM D648 |
| Vicat Softening Temp, Rate B/50 | 206 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 203 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 204 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate B/120 | 194 | °C | ASTM D1525 |
| CTE, 23°C to 60°C, flow | 2.2E-05 | 1/°C | ASTM E831 |
| CTE, 23°C to 60°C, xflow | 1.0E-05 | 1/°C | ASTM E831 |
| Ball Pressure Test, 125°C +/- 2°C | Passes | - | IEC 60695-10-2 |
| Relative Temp Index, Elec | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.