NORYL™ Resin TP0140IF

NORYL TP0140IF resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade exhibits high transparency, high heat resistance, high ductility, very low water absorption and dimensional stability. TP0140IF carries FDA food contact compliance and No PFAS and Bisphenol A intentionally added. Target applications are small appliances, steamer, water bottles, cutlery and other food contact applications.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Dimensional stability
Food contact
Hydrolytic Stability
Low Corrosivity
Low Moisture Absorption
Low Specific Gravity
Low Warpage
No PFAS intentionally added
Transparent/Translucent

Industry

Material previously used in

Commercial Appliance
Consumer Goods
Food & Beverage

Applications

Possible usage of material

Bottles
Commercial Appliance
Food Container
Small Appliance

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	45	J/m	ASTM D256
Izod Impact, unnotched, 23°C	660	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	4.3	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	90 - 100	°C
Drying Time	2 - 4	Hrs
Drying Time (Cumulative)	6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	290 - 310	°C
Nozzle Temperature	290 - 310	°C
Front - Zone 3 Temperature	280 - 310	°C
Middle - Zone 2 Temperature	270 - 305	°C
Rear - Zone 1 Temperature	265 - 300	°C
Mold Temperature	80 - 110	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	20 - 100	rpm
Shot to Cylinder Size	30 - 70	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	70	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	48	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5.3	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	15	%	ASTM D638
Tensile Modulus, 50 mm/min	2280	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	105	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2350	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	73.5	MPa	ISO 527
Tensile Stress, break, 50 mm/min	48.5	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5.1	%	ISO 527
Tensile Strain, break, 50 mm/min	12	%	ISO 527
Tensile Modulus, 1 mm/min	2470	MPa	ISO 527
Flexural Strength, 2 mm/min	102	MPa	ISO 178
Flexural Modulus, 2 mm/min	2380	MPa	ISO 178

OPTICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Light Transmission at 2.0 mm	82	%	ASTM D1003
Haze, 2mm	2	%	SABIC method
Yellowness Index	45	-	ASTM D1925

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.05	-	ASTM D792
Melt Flow Rate, 300°C/5.0 kgf	16	g/10 min	ASTM D1238
Water Absorption, (23°C/24hrs)	0.06	%	ISO 62-1
Mold Shrinkage, flow, 3.2 mm	0.9 - 1.1	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	1.0 - 1.2	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	139	°C	ASTM D648
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	138	°C	ISO 75/Af

Register for High value Multi-Point Data