IMPACT
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 31 | J/m | ASTM D256 |
NORYL TP1000 resin is a high heat, transparent, hydro-stable, non-reinforced, high-purity blend of polyphenylene ether (PPE) + general purpose polystyrene (GPPS). This injection moldable material is FDA food contact compliant and black spec controlled, which can be an excellent candidate for food contact, small appliance housings, and for industrial additive use.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 31 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 110 - 120 | °C | |
Drying Time | 3 - 4 | Hrs | |
Drying Time (Cumulative) | 8 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 300 - 325 | °C | |
Nozzle Temperature | 300 - 325 | °C | |
Front - Zone 3 Temperature | 290 - 325 | °C | |
Middle - Zone 2 Temperature | 275 - 320 | °C | |
Rear - Zone 1 Temperature | 265 - 315 | °C | |
Mold Temperature | 80 - 110 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 20 - 100 | rpm | |
Shot to Cylinder Size | 30 - 70 | % |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield | 81 | MPa | SABIC - Japan Method |
Tensile Strain, break | 80 | % | SABIC - Japan Method |
Flexural Stress | 119 | MPa | ASTM D790 |
Flexural Modulus | 2800 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.08 | - | ASTM D792 |
Water Absorption, (23°C/24hrs) | 0.07 | % | ASTM D570 |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate, 300°C/5.0 kgf | 14.8 | g/10 min | ASTM D1238 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 6.4 mm, unannealed | 149 | °C | ASTM D648 |
CTE, -30°C to 30°C | 6.00E-05 | 1/°C | TMA |