ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 2.0E+16 | Ω.cm | ASTM D257 |
Surface Resistivity | 1.1E+16 | Ω | ASTM D257 |
Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A |
NORYL V0150TW resin is an unreinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V0 at 1.0mm, 5VA at 1.5mm along with a UL746C Outdoor Suitability rating of F1. NORYL V0150TW resin exhibits high impact strength, good dimensional stability, high heat resistance, strong electrical performance and very low specific gravity. NORYL V0150TW resin is intended for parts that are exposed to tough outdoor environments such as Solar / Photovoltaic (PV) junction boxes and micro-invertors, and other electrical components requiring thin wall frame retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 2.0E+16 | Ω.cm | ASTM D257 |
Surface Resistivity | 1.1E+16 | Ω | ASTM D257 |
Comparative Tracking Index (UL) {PLC} | 2 | PLC Code | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | ≥1.0 | mm | UL 94 |
UL Recognized, 94-5VA Flame Class Rating | ≥1.5 | mm | UL 94 |
Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
Glow Wire Ignitability Temperature, 3.0 mm | 825 | °C | IEC 60695-2-13 |
UV-light, water exposure/immersion | f1 | - | UL 746C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 202 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 86 | J/m | ASTM D256 |
Izod Impact, unnotched, 23°C | 2160 | J/m | ASTM D4812 |
Izod Impact, unnotched, -30°C | 1520 | J/m | ASTM D4812 |
Izod Impact, notched 80*10*4 +23°C | 15.9 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 7.9 | kJ/m² | ISO 180/1A |
Izod Impact, unnotched 80*10*4 +23°C | 131 | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*4 -30°C | 115 | kJ/m² | ISO 180/1U |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 18.4 | kJ/m² | ISO 179/1eA |
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 6.1 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 95 | kJ/m² | ISO 179/1eU |
Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 95 | kJ/m² | ISO 179/1eU |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 100 - 120 | °C | |
Drying Time | 3 - 5 | Hrs | |
Melt Temperature | 280 - 330 | °C | |
Nozzle Temperature | 250 - 330 | °C | |
Front - Zone 3 Temperature | 280 - 330 | °C | |
Middle - Zone 2 Temperature | 280 - 330 | °C | |
Rear - Zone 1 Temperature | 280 - 330 | °C | |
Hopper Temperature | 70 - 140 | °C | |
Mold Temperature | 30 - 100 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 5 mm/min | 69 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 51 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 4.6 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 16 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 2584 | MPa | ASTM D638 |
Flexural Stress at 5% strain, 1.3 mm/min, 50 mm span | 108 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2590 | MPa | ASTM D790 |
Tensile Stress, yield, 5 mm/min | 70 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 51 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 4.5 | % | ISO 527 |
Tensile Strain, break, 5 mm/min | 24.7 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2614 | MPa | ISO 527 |
Flexural Strength, 2 mm/min | 117 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2556 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.1 | - | ASTM D792 |
Density | 1.1 | g/cm³ | ISO 1183 |
Melt Flow Rate, 300°C/5.0 kgf | 14.5 | g/10 min | ASTM D1238 |
Melt Volume Rate, MVR at 300°C/5.0 kg | 10.7 | cm³/10 min | ISO 1133 |
Moisture Absorption (23°C / 50% RH) | 0.07 | % | ISO 62 |
Mold Shrinkage, flow, 3.2 mm | 1.01 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 1.08 | % | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 149 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 133 | °C | ASTM D648 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 149 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 131 | °C | ISO 75/Af |
Vicat Softening Temp, Rate A/50 | 165 | °C | ASTM D1525 |
Vicat Softening Temp, Rate B/50 | 153 | °C | ASTM D1525 |
Vicat Softening Temp, Rate A/50 | 164 | °C | ISO 306 |
Vicat Softening Temp, Rate B/50 | 153 | °C | ISO 306 |
CTE, -40°C to 40°C, flow | 7.2E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 7.6E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 7.2E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 7.4E-05 | 1/°C | ISO 11359-2 |
Relative Temp Index, Elec | 110 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 115 | °C | UL 746B |