SILTEM™ Resin HUSTM1500

Sustainable Grade

SILTEM™ HUSTM1500 resin is a flexible polyetherimide(PEI)-siloxane copolymer. The intended use for this material is in medical devices and pharmaceutical applications. The material is biocompatible (ISO 10993) and Healthcare management of change applies. The material is RoHS compliant and offers a halogen free (according VDE 0472) flame retardant solution that also offers low smoke emission and toxicity. It is an amber colored transparent material that can be self-colored and easily processed on conventional processing equipment. The material may be used for extrusion of e.g. tubing, catheters, cannulas, as well as flexible injection molded parts.

ISCC+ certified renewable bio-based solutions can be made available for this grade.

The grade listed in this document does not contain PFAS intentionally added during Seller's manufacturing process and is not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Product Family

ULTEM™ RESIN FAMILY OF HIGH HEAT SOLUTIONS

Polymer Family

Polyetherimide (PEI)

Processing Technology

Compounding Extrusion
Film Extrusion
Injection Molding
Profile Extrusion
Extrusion
Compression molding
Injection compression molding
Pipe extrusion
Foam Extrusion

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Biocompatability-ISO10993
Chemical Resistance
Dielectrics
Dimensional stability
Flame Retardant
Flexible
Good Processability
Healthcare
Healthcare/Formula lock
High Flow
High temperature resistance
IR Transparent
Low Corrosivity
Low Moisture Absorption
Low Smoke and Toxicity
Low Specific Gravity
No PFAS intentionally added
Non Cl/Br flame retardant
Non halogenated flame retardant
Sustainable (bio-based offerings)
Thin Wall
Transparent/Translucent

Industry

Material previously used in

General Healthcare
Patient Testing
Pharmaceutical Packaging and Drug Delivery
Surgical devices

Applications

Possible usage of material

Pharmaceutical Packaging & Drug Delivery
Surgical Devices
Healthcare
healthcare device

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

COMBUSTION CORROSIVITY

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Corrosion, 1 hr (2500 angstroms max)	40	angstrom	ASTM E5.2170
Corrosion, 24 hrs	122	angstrom	ASTM E5.2170
Corrosion, 6 days	183	angstrom	ASTM E5.2170

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	4.7E+14	Ω.cm	IEC 60093
Surface Resistivity, ROA	1.E+15	Ω	IEC 60093
Dielectric Strength, in oil, 3.2 mm	19	kV/mm	IEC 60243-1
Relative Permittivity, 100 Hz	3	-	IEC 60250
Dissipation Factor, 100 Hz	0.0091	-	IEC 60250
Volume Resistivity	4.1E+16	Ω.cm	ASTM D257
Surface Resistivity	1.E+15	Ω	ASTM D257
Dielectric Strength, in air, 3.2 mm	16.1	kV/mm	ASTM D149
Dielectric Strength, in oil, 3.2 mm	16.3	kV/mm	ASTM D149
Relative Permittivity, 50/60 Hz	3.01	-	ASTM D150
Relative Permittivity, 100 kHz	2.7	-	ASTM D150
Dissipation Factor, 50/60 Hz	0.01	-	ASTM D150
Dissipation Factor, 100 kHz	0.0056	-	ASTM D150
Comparative Tracking Index	175	V	IEC 60112

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Compliant, 94V-1 Flame Class Rating	1.6	mm	UL 94 by SABIC-IP
Glow Wire Flammability Index 960°C, passes at	3.2	mm	IEC 60695-2-12
Oxygen Index (LOI)	48	%	ISO 4589
OSU peak heat release rate (5 minute test)	140	kW/m²	FAR 25.853
Oxygen Index (LOI)	46	%	ASTM D2863

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, unnotched 80104 +23°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	25	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	15	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100 - 110	°C
Drying Time	6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	300 - 320	°C
Nozzle Temperature	300 - 320	°C
Front - Zone 3 Temperature	295 - 315	°C
Middle - Zone 2 Temperature	295 - 315	°C
Rear - Zone 1 Temperature	295 - 315	°C
Mold Temperature	65 - 95	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	50 - 100	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Taber Abrasion, CS-17, 1 kg	60	mg/1000cy	SABIC method
Tensile Stress, yield, 50 mm/min	20	MPa	ISO 527
Tensile Stress, break, 50 mm/min	25	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	15	%	ISO 527
Tensile Strain, break, 50 mm/min	110	%	ISO 527
Tensile Modulus, 1 mm/min	590	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	20	MPa	ISO 178
Flexural Stress, break, 2 mm/min	18	MPa	ISO 178
Flexural Modulus, 2 mm/min	470	MPa	ISO 178
Tensile Stress, yld, Type I, 50 mm/min	28	MPa	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	100	%	ASTM D638
Flexural Modulus, 2.6 mm/min, 100 mm span	380	MPa	ASTM D790
Taber Abrasion, CS-17, 1 kg	26	mg/1000cy	ASTM D1044

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Mold Shrinkage, flow	1.35	%	SABIC method
Mold Shrinkage, xflow	1.43	%	SABIC method
Mold Shrinkage on Tensile Bar, flow	1.2 - 1.4	%	SABIC method
Density	1.18	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)	0.5	%	ISO 62-1
Melt Volume Rate, MVR at 320°C/2.16 kg	8	cm³/10 min	ISO 1133
Specific Gravity	1.18	-	ASTM D792
Moisture Absorption (est)	0.3	%	ASTM D570
Melt Flow Rate, 295°C/6.6 kgf	12	g/10 min	ASTM D1238
Matrix Tg	168	°C	DMA
Halogen Content	0	%	SABIC method

PROFILE EXTRUSION

PROPERTIES	TYPICAL VALUES	UNITS
Barrel - Zone 1 Temperature	280 - 290	°C
Barrel - Zone 2 Temperature	300 - 310	°C
Barrel - Zone 3 Temperature	310 - 320	°C
Barrel - Zone 4 Temperature	310 - 325	°C
Hopper Temperature	60 - 100	°C
Adapter Temperature	315 - 325	°C
Die Temperature	300 - 320	°C
Calibrator Temperature	60 - 80	°C

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
CTE, 23°C to 80°C, flow	1.1E-04	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	9.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 75°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate B/50	75	°C	ISO 306
Vicat Softening Temp, Rate B/120	78	°C	ISO 306

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES