ULTEM™ Resin 1010UCL

ULTEM 1010UCL resin is an amorphous, transparent polyetherimide (PEI) thermoplastic offering enhanced flow and a glass transition temperature (Tg) of 217°C. 1010UCL offers the same performance as ULTEM 1010 resin and offers further enhanced cleanliness control for (optical) applications.

The natural (uncolored) version of this grade is compliant with RoHS and also with Halogen Free standards as IEC 61249-2-21 and e.g. IPC 4101E. For colored versions, compliance needs to be checked case by case.

Product Family

ULTEM™ RESIN FAMILY OF HIGH HEAT SOLUTIONS

Polymer Family

Polyetherimide (PEI)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Chemical Resistance
Creep resistant
Dielectrics
Dimensional stability
Electroplatable
Flame Retardant
Good Processability
High Flow
High stiffness/Strength
High temperature resistance
Hydrolytic Stability
IR Transparent
Low Shrinkage
Low Smoke and Toxicity
Low Warpage
No PFAS intentionally added
Thin Wall
Transparent/Translucent

Industry

Material previously used in

Electrical
Eyewear
Mobile Phone - Computer - Tablets
Wireless Communication

Applications

Possible usage of material

Aerospace
Air Cabin Interiors
Aircraft Seating
Audio
Auto Aftermarket
Auto Electrical
Building Accessory
Circuit Protection
Coffee Maker/Espresso Machine
Commercial Storage/Cookware
Composite
Cooking Range
Data Management
Data Transfer
Dishwasher
Displays
Document Handling
Electronic Components
Electronic Material Handling
Electronics
Enclosure/Housing/Cover
Enclosures
Engine Cooling System
Exterior Rail Components
Exterior Trim
Eyeglasses
Fluid Delivery
Fog Lamp
Food Container
Food Processor
Forward Lighting
Front Grille
Fuel Cell
Gas/Electric Oven
Humidity Control
Ignition System
Individual Equipment
Industrial Material Handling
Interior Rail Components
Lab Ware and Clinical Diagnostics
LED Lighting
Lighting
Medical Device
Meter Gas
Monitoring and Imaging
Non-LED Lighting
Oil/Gas
OLED
Personal Care
Personal Computing
Pharmaceutical Packaging & Drug Delivery
Photo/Video Camera
Photovoltaic Components
Pipe/Fitting
Power Manangement
Rear/Signal Lighting
Respiratory
Safety Glasses
Security/Detection
Semiconductor
Small Appliance
Smart/ID Card
Sunglasses
Surgical Devices
Surgical Tray
Tray
Water Treatment/Filtration
Wearables
Wireless Communications
Wiring Devices
Adhesives
Wire & cable

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	1.E+15	Ω.cm	IEC 60093
Surface Resistivity, ROA	>1.E+15	Ω	IEC 60093
Dielectric Strength, in oil, 0.8 mm	33	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 1.6 mm	25	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 3.2 mm	16	kV/mm	IEC 60243-1
Relative Permittivity, 1 MHz	2.9	-	IEC 60250
Dissipation Factor, 50/60 Hz	0.0005	-	IEC 60250
Dissipation Factor, 1 MHz	0.006	-	IEC 60250
Dissipation Factor, 2450 MHz	0.0025	-	IEC 60250
Relative Permittivity, 50/60 Hz	2.9	-	IEC 60250
Volume Resistivity	1.E+17	Ω.cm	ASTM D257
Dielectric Strength, in air, 1.6 mm	32.7	kV/mm	ASTM D149
Dielectric Strength, in oil, 1.6 mm	28.0	kV/mm	ASTM D149
Relative Permittivity, 1 kHz	3.15	-	ASTM D150
Dissipation Factor, 1 kHz	0.0013	-	ASTM D150
Dissipation Factor, 2450 MHz	0.0025	-	ASTM D150

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, unnotched 80104 +23°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	5	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	5	kJ/m²	ISO 180/1A
Izod Impact, unnotched, 23°C	1335	J/m	ASTM D4812
Izod Impact, notched, 23°C	32	J/m	ASTM D256
Izod Impact, Reverse Notched, 3.2 mm	1174	J/m	ASTM D256
Gardner, 23°C	33	J	ASTM D3029

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	150	°C
Drying Time	4 - 6	Hrs
Drying Time (Cumulative)	24	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	350 - 400	°C
Nozzle Temperature	345 - 400	°C
Front - Zone 3 Temperature	345 - 400	°C
Middle - Zone 2 Temperature	340 - 400	°C
Rear - Zone 1 Temperature	330 - 400	°C
Mold Temperature	135 - 165	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield, 50 mm/min	105	MPa	ISO 527
Tensile Stress, break, 50 mm/min	85	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	6	%	ISO 527
Tensile Strain, break, 50 mm/min	60	%	ISO 527
Tensile Modulus, 1 mm/min	3200	MPa	ISO 527
Flexural Stress, yield, 2 mm/min	160	MPa	ISO 178
Flexural Modulus, 2 mm/min	3300	MPa	ISO 178
Ball Indentation Hardness, H358/30	140	MPa	ISO 2039-1
Taber Abrasion, CS-17, 1 kg	10	mg/1000cy	SABIC method
Tensile Stress, yld, Type I, 5 mm/min	110	MPa	ASTM D638
Tensile Strain, yld, Type I, 5 mm/min	7	%	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	60	%	ASTM D638
Tensile Modulus, 5 mm/min	3580	MPa	ASTM D638
Flexural Stress, yld, 2.6 mm/min, 100 mm span	165	MPa	ASTM D790
Flexural Modulus, 2.6 mm/min, 100 mm span	3510	MPa	ASTM D790
Hardness, Rockwell M	109	-	ASTM D785
Taber Abrasion, CS-17, 1 kg	10	mg/1000cy	ASTM D1044

OPTICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Light Transmission
– at 1.0 mm and 850 nm	88	%	ASTM D1003
– at 1.0 mm and 1350 nm	89	%	ASTM D1003
Refractive Index
– at 850 nm	1.639	-	ISO 489
– at 1350 nm	1.626	-	ISO 489
Abbe number	21	-	ISO 489

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.27	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)	1.25	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.7	%	ISO 62
Melt Volume Rate, MVR at 340°C/5.0 kg	13	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 360°C/5.0 kg	25	cm³/10 min	ISO 1133
Specific Gravity	1.27	-	ASTM D792
Water Absorption, (23°C/24hrs)	0.25	%	ASTM D570
Water Absorption, (23°C/Saturated)	1.25	%	ASTM D570
Mold Shrinkage, flow, 3.2 mm	0.5 - 0.7	%	SABIC method
Melt Flow Rate, 337°C/6.6 kgf	17.8	g/10 min	ASTM D1238

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Thermal Conductivity	0.21	W/m-°C	ISO 8302
CTE, 23°C to 150°C, flow	5.2E-05	1/°C	ISO 11359-2
CTE, 23°C to 150°C, xflow	5.2E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate A/50	215	°C	ISO 306
Vicat Softening Temp, Rate B/50	211	°C	ISO 306
Vicat Softening Temp, Rate B/120	212	°C	ISO 306
*HDT/Be, 0.45MPa Edgew 120104 sp=100mm*	200	°C	ISO 75/Be
*HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm*	190	°C	ISO 75/Ae
Vicat Softening Temp, Rate B/50	218	°C	ASTM D1525
HDT, 0.45 MPa, 6.4 mm, unannealed	207	°C	ASTM D648
HDT, 1.82 MPa, 6.4 mm, unannealed	198	°C	ASTM D648
CTE, -20°C to 150°C, flow	5.2E-05	1/°C	ASTM E831
Thermal Conductivity	0.22	W/m-°C	ASTM C177

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES