Sustainable Grade
2210GCR3 resin grade is 30% PCR (Post Consumer Recycle) combined with bio-based polyetherimide solutions. 20% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ISCC+ certified renewable bio-based solutions are available for this grade.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 69 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 544 | J/m | ASTM D4812 |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 140 - 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Drying Time (Cumulative) | 24 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 350 - 400 | °C | |
| Nozzle Temperature | 345 - 400 | °C | |
| Front - Zone 3 Temperature | 345 - 400 | °C | |
| Middle - Zone 2 Temperature | 345 - 400 | °C | |
| Rear - Zone 1 Temperature | 330 - 400 | °C | |
| Mold Temperature | 135 - 165 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 50 mm/min | 143 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 4 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 7040 | MPa | ASTM D638 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 231 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7072 | MPa | ASTM D790 |
| Tensile Stress, break, 50 mm/min | 148 | MPa | ISO 527 |
| Tensile Strain, break, 50 mm/min | 3.6 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 7020 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 227 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 7030 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.42 | - | ASTM D792 |
| Density | 1.42 | g/cm³ | ISO 1183 |
| Melt Flow Rate | |||
| – 337°C/6.7 kgf | 10 | g/10 min | ASTM D1238 |
| – 350°C/2.16 kgf | 6.1 | g/10 min | ASTM D1238 |
| Water Absorption, (23°C/24hrs) | 0.19 | % | ASTM D570 |
| Moisture Absorption, (23°C/50% RH/24hrs) | 0.06 | % | ISO 62-4 |
| Mold Shrinkage, flow | 0.33 | % | SABIC method |
| Mold Shrinkage, xflow | 0.59 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 211 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 208 | °C | ASTM D648 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 214 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 208 | °C | ISO 75/Af |
| CTE, 23°C to 150°C, flow | 2.1E-05 | 1/°C | ASTM E831 |
| CTE, 23°C to 150°C, xflow | 5.0E-05 | 1/°C | ASTM E831 |
| CTE, 23°C to 150°C, flow | 2.0E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 5.0E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate B/120 | 215 | °C | ASTM D1525 |
| Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 217 | °C | ISO 306 |