ULTEM™ Resin 2300R

Sustainable Grade

ULTEM 2300R resin is a standard flow 30% glass fiber reinforced polyetherimide resin with an added internal mold release. The material is RoHS compliant and is intrinsically flame retardant without the use of FR modifiers and offers UL94 V0 and 5VA ratings. The material may offer excellent dimension stability, strength, stiffness and creep resistance up to high temperature due to its high glass transition temperature of 217°C. The material is opaque and can be custom colored.

ISCC+ certified renewable bio-based solutions are available for this grade via differentiated color nomenclature.

Product Family

ULTEM™ RESIN FAMILY OF HIGH HEAT SOLUTIONS

Polymer Family

Polyetherimide (PEI)

Processing Technology

Large Format Additive Manufacturing (LFAM)
Sheet extrusion
Injection Molding
Profile Extrusion
Extrusion
Compression molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Chemical Resistance
Creep resistant
Dielectrics
Dimensional stability
Electroplatable
Enhanced mold release
Flame Retardant
High stiffness/Strength
High temperature resistance
Hydrolytic Stability
Low Shrinkage
Low Smoke and Toxicity
Low Warpage
No PFAS intentionally added
Non halogenated flame retardant
Sustainable (bio-based offerings)

Industry

Material previously used in

Aerospace
Automotive Under the Hood
Building Component
Circuit Boards/Additives
Commercial Appliance
Consumer Goods
Drone Solutions
Electrical
Energy Management
Eyewear
Furniture
General Healthcare
Heavy Truck
Home Appliances
Industrial Packaging
Lighting
Material Handling
Mobile Phone - Computer - Tablets
Motorcycle
Patient Testing
Personal Accessory
Personal and Professional Hygiene
Pharmaceutical Packaging and Drug Delivery
Printer Copier
Rail
Recreational/Specialty Vehicles
Speaker - Earphone
Sport/Leisure
Surgical devices
Textile
Water Management
Wireless Communication

Applications

Possible usage of material

Air Cabin Interiors
Aircraft Seating
Auto Aftermarket
Electronic Components
Medical Facility Infrastructure
Surgical Devices

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	1E+15	Ω.cm	IEC 60093
Surface Resistivity, ROA	>1E+15	Ω	IEC 60093
Dielectric Strength, in oil, 0.8 mm	35	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 1.6 mm	26	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 3.2 mm	15	kV/mm	IEC 60243-1
Relative Permittivity, 50/60 Hz	3.3	-	IEC 60250
Relative Permittivity, 1 MHz	3.4	-	IEC 60250
Dissipation Factor, 50/60 Hz	0.0016	-	IEC 60250
Dissipation Factor, 1 MHz	0.0025	-	IEC 60250
Dielectric Constant
– at 1.1 GHz	3.51	-	-
– at 5 GHz	3.51	-	-
– at 10 GHz	3.51	-	-
Dissipation Factor
– at 1.1 GHz	0.0029	-	-
– at 5 GHz	0.0029	-	-
– at 10 GHz	0.0029	-	-
Comparative Tracking Index	150	V	IEC 60112
Comparative Tracking Index, M	100	V	IEC 60112
Volume Resistivity	3.E+16	Ω.cm	ASTM D257
Dielectric Strength, in air, 1.6 mm	24.8	kV/mm	ASTM D149
Dielectric Strength, in oil, 1.6 mm	30.3	kV/mm	ASTM D149
Relative Permittivity, 1 kHz	3.7	-	ASTM D150
Dissipation Factor, 1 kHz	0.0015	-	ASTM D150
Comparative Tracking Index (UL) {PLC}	4	PLC Code	UL 746A
Hot-Wire Ignition (HWI), PLC 1	≥3	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 3	≥1.5	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 3	≥1.5	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 4	≥3	mm	UL 746A
High Voltage Arc Track Rate {PLC}	3	PLC Code	UL 746A
Arc Resistance, Tungsten {PLC}	6	PLC Code	ASTM D495

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Yellow Card Link 2	View	-	-
UL Recognized, 94-5VA Flame Class Rating	≥1.2	mm	UL 94
UL Recognized, 94V-0 Flame Class Rating	0.25	mm	UL 94
Glow Wire Ignitability Temperature, 2.0 mm	900	°C	IEC 60695-2-13
Glow Wire Flammability Index, 2.0 mm	960	°C	IEC 60695-2-12
UV-light, water exposure/immersion	F1	-	UL 746C
Oxygen Index (LOI)	48	%	ISO 4589
Oxygen Index (LOI)	50	%	ASTM D2863
NBS Smoke Density, Flaming, Ds 4 min	1.6	-	ASTM E662

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	10	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	10	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	40	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	40	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	10	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	10	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	40	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	40	kJ/m²	ISO 179/1eU
Izod Impact, notched, 23°C	90	J/m	ASTM D256
Izod Impact, notched, -30°C	80	J/m	ASTM D256
Izod Impact, Reverse Notched, 3.2 mm	470	J/m	ASTM D256
Izod Impact, unnotched, 23°C	600	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	600	J/m	ASTM D4812

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	150	°C
Drying Time	4 - 6	Hrs
Drying Time (Cumulative)	24	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	350 - 410	°C
Nozzle Temperature	345 - 410	°C
Front - Zone 3 Temperature	345 - 420	°C
Middle - Zone 2 Temperature	340 - 410	°C
Rear - Zone 1 Temperature	330 - 400	°C
Hopper Temperature	80 - 120	°C
Mold Temperature	135 - 180	°C
Shot to Cylinder Size	40 - 60	%
Vent Depth	0.025 - 0.076	mm
Screw Speed	40 - 70	rpm
Screw speed (Circumferential speed)	0.15 - 0.25	m/s
Back Pressure	0.3 - 1.5	MPa

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	175	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.4	%	ISO 527
Tensile Modulus, 1 mm/min	10500	MPa	ISO 527
Flexural Stress, break, 2 mm/min	240	MPa	ISO 178
Flexural Modulus, 2 mm/min	9600	MPa	ISO 178
Ball Indentation Hardness, H358/30	165	MPa	ISO 2039-1
Hardness, Rockwell M	110	-	ISO 2039-2
Taber Abrasion, CS-17, 1 kg	20	mg/1000cy	SABIC method
Tensile Stress, brk, Type I, 5 mm/min	175	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2.5	%	ASTM D638
Tensile Modulus, 5 mm/min	10400	MPa	ASTM D638
Flexural Stress, brk, 2.6 mm/min, 100 mm span	230	MPa	ASTM D790
Flexural Modulus, 2.6 mm/min, 100 mm span	9400	MPa	ASTM D790
Flexural Stress, brk, 1.3 mm/min, 50 mm span	250	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	9700	MPa	ASTM D790
Hardness, Rockwell M	114	-	ASTM D785

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.51	g/cm³	ISO 1183
Moisture Absorption, (23°C/50% RH/24hrs)	0.1	%	ISO 62-4
Moisture Absorption, (23°C/50% RH/Equilibrium)	0.6	%	ISO 62-4
Water Absorption, (23°C/24hrs)	0.16	%	ISO 62-1
Water Absorption, (23°C/saturated)	0.9	%	ISO 62-1
Melt Volume Rate, MVR at 360°C/5.0 kg	6	cm³/10 min	ISO 1133
Specific Gravity	1.51	-	ASTM D792
Water Absorption, (23°C/24hrs)	0.16	%	ASTM D570
Water Absorption, (23°C/Saturated)	0.9	%	ASTM D570
Melt Flow Rate, 337°C/6.6 kgf	5	g/10 min	ASTM D1238
Mold Shrinkage, flow, 3.2 mm	0.2 - 0.4	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	215	°C	ISO 75/Bf
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	210	°C	ISO 75/Af
Vicat Softening Temp, Rate A/50	225	°C	ISO 306
Vicat Softening Temp, Rate B/120	220	°C	ISO 306
Vicat Softening Temp, Rate B/50	213	°C	ISO 306
CTE, -40°C to 150°C, flow	1.8E-05	1/°C	ISO 11359-2
CTE, -40°C to 150°C, xflow	4.8E-05	1/°C	ISO 11359-2
Thermal Conductivity	0.31	W/m-°C	ISO 8302
Ball Pressure Test, 125°C +/- 2°C	PASS	-	IEC 60695-10-2
HDT, 0.45 MPa, 3.2 mm, unannealed	215	°C	ASTM D648
HDT, 0.45 MPa, 6.4 mm, unannealed	212	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	211	°C	ASTM D648
HDT, 1.82 MPa, 6.4 mm, unannealed	210	°C	ASTM D648
CTE, -20°C to 150°C, flow	1.8E-05	1/°C	ASTM E831
CTE, -20°C to 150°C, xflow	4.8E-05	1/°C	ASTM E831
Relative Temp Index, Elec	180	°C	UL 746B
Relative Temp Index, Mech w/impact	170	°C	UL 746B
Relative Temp Index, Mech w/o impact	180	°C	UL 746B

THIS SITE USES COOKIES

ULTEM™ Resin 2300R

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Curve Data

CAE Cards

Register for High value Multi-Point Data

THIS SITE USES COOKIES

ULTEM™ Resin 2300R

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

Curve Data

CAE Cards

Related Documents

Technical Data Sheets