ULTEM 2310EPR resin is a further improved flow 30% glass fiber reinforced polyetherimide resin with an added internal mold release. The material is RoHS compliant and is intrinsically flame retardant without the use of FR modifiers and offers UL94 V0 and 5VA ratings. The material may offer excellent dimension stability, strength, stiffness and creep resistance up to high temperature due to its high glass transition temperature of 217°C. Beside enhanced flow the material offers enhanced metal adhesion in Electroplated applications. The material is opaque.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 1 | ≥3 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 2 | ≥1.5 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 3 | ≥0.75 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 4 | ≥0.4 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 4 | ≥0.4 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 6 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | 0.4 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 450 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 85 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy, 23°C | 9 | J | ASTM D3763 |
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 10 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 10 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m² | ISO 179/1eA |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 30 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 35 | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Drying Time (Cumulative) | 24 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 350 - 400 | °C | |
| Nozzle Temperature | 345 - 400 | °C | |
| Front - Zone 3 Temperature | 345 - 400 | °C | |
| Middle - Zone 2 Temperature | 340 - 400 | °C | |
| Rear - Zone 1 Temperature | 330 - 400 | °C | |
| Mold Temperature | 135 - 165 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 158 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 158 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 5 mm/min | 2.1 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.1 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 8580 | MPa | ASTM D638 |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 228 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 9140 | MPa | ASTM D790 |
| Tensile Stress, yield, 5 mm/min | 160 | MPa | ISO 527 |
| Tensile Stress, break, 5 mm/min | 160 | MPa | ISO 527 |
| Tensile Strain, yield, 5 mm/min | 2 | % | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 8970 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 210 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 9500 | MPa | ISO 178 |
| Ball Indentation Hardness, H358/30 | 160 | MPa | ISO 2039-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.48 | - | ASTM D792 |
| Mold Shrinkage on Tensile Bar, flow | 0.3 - 0.5 | % | SABIC method |
| Mold Shrinkage, flow, 3.2 mm | 0.4 - 0.6 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 0.4 - 0.6 | % | SABIC method |
| Melt Flow Rate, 337°C/6.6 kgf | 11 | g/10 min | ASTM D1238 |
| Density | 1.48 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.9 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.5 | % | ISO 62 |
| Melt Volume Rate, MVR at 360°C/5.0 kg | 12 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Vicat Softening Temp, Rate B/50 | 217 | °C | ASTM D1525 |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 205 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 201 | °C | ASTM D648 |
| HDT, 0.45 MPa, 6.4 mm, unannealed | 208 | °C | ASTM D648 |
| HDT, 1.82 MPa, 6.4 mm, unannealed | 205 | °C | ASTM D648 |
| CTE, -40°C to 150°C, flow | 1.8E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 150°C, xflow | 3.E-05 | 1/°C | ASTM E831 |
| Thermal Conductivity | 0.31 | W/m-°C | ISO 8302 |
| CTE, 23°C to 150°C, flow | 1.8E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 3.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASS | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/50 | 212 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 214 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 207 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 196 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.