ULTEM™ Resin 2400F

Sustainable Grade

40% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 listing. US FDA and European Food Contact approved. Effective June, 2007 this grade will no longer be supported with biocompatibility information and should not be used for medical applications which require biocompatibility. Alternative grade HU2400.

Product Family

ULTEM™ RESIN FAMILY OF HIGH HEAT SOLUTIONS

Polymer Family

Polyetherimide (PEI)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Europe

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Chemical Resistance
Creep resistant
Dimensional stability
Electroplatable
Flame Retardant
Food contact
High stiffness/Strength
High temperature resistance
Hydrolytic Stability
Low Shrinkage
Low Smoke and Toxicity
Low Warpage
No PFAS intentionally added
Non halogenated flame retardant
Sustainable (bio-based offerings)

Industry

Material previously used in

Aerospace
Automotive Under the Hood
Building Component
Circuit Boards/Additives
Commercial Appliance
Consumer Goods
Drone Solutions
Electrical
Energy Management
Eyewear
Furniture
General Healthcare
Heavy Truck
Home Appliances
Industrial Packaging
Lighting
Material Handling
Mobile Phone - Computer - Tablets
Motorcycle
Patient Testing
Personal Accessory
Personal and Professional Hygiene
Pharmaceutical Packaging and Drug Delivery
Printer Copier
Rail
Recreational/Specialty Vehicles
Speaker - Earphone
Sport/Leisure
Surgical devices
Textile
Water Management
Wireless Communication

Applications

Possible usage of material

Coffee Maker/Espresso Machine
Individual Equipment
Small Appliance

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	1.E+15	Ω.cm	IEC 60093
Surface Resistivity, ROA	>1.E+15	Ω	IEC 60093
Dielectric Strength, in oil, 0.8 mm	35	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 1.6 mm	26	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 3.2 mm	16	kV/mm	IEC 60243-1
Relative Permittivity, 1 MHz	3.1	-	IEC 60250
Dissipation Factor, 50/60 Hz	0.0025	-	IEC 60250
Dissipation Factor, 1 MHz	0.0019	-	IEC 60250
Comparative Tracking Index	150	V	IEC 60112
Comparative Tracking Index, M	100	V	IEC 60112
Relative Permittivity, 50/60 Hz	3.5	-	IEC 60250
Comparative Tracking Index (UL) {PLC}	5	PLC Code	UL 746A
Hot-Wire Ignition (HWI), PLC 0	≥1.5	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 4	≥1.5	mm	UL 746A
High Voltage Arc Track Rate {PLC}	4	PLC Code	UL 746A
Arc Resistance, Tungsten {PLC}	5	PLC Code	ASTM D495

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	0.25	mm	UL 94
Glow Wire Ignitability Temperature, 1.5 mm	875	°C	IEC 60695-2-13
Glow Wire Ignitability Temperature, 1.0 mm	850	°C	IEC 60695-2-13
Glow Wire Flammability Index, 1.5 mm	960	°C	IEC 60695-2-12
Glow Wire Flammability Index, 1.0 mm	960	°C	IEC 60695-2-12
Oxygen Index (LOI)	48	%	ISO 4589

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, unnotched 80104 +23°C*	35	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	35	kJ/m²	ISO 180/1U
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	40	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	40	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	150	°C
Drying Time	4 - 6	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	370 - 410	°C
Nozzle Temperature	370 - 410	°C
Front - Zone 3 Temperature	380 - 420	°C
Middle - Zone 2 Temperature	370 - 410	°C
Rear - Zone 1 Temperature	350 - 390	°C
Hopper Temperature	80 - 100	°C
Mold Temperature	140 - 180	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Taber Abrasion, CS-17, 1 kg	20	mg/1000cy	SABIC method
Tensile Stress, break, 5 mm/min	180	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2	%	ISO 527
Tensile Modulus, 1 mm/min	11500	MPa	ISO 527
Flexural Stress, break, 2 mm/min	240	MPa	ISO 178
Flexural Modulus, 2 mm/min	10000	MPa	ISO 178
Ball Indentation Hardness, H358/30	170	MPa	ISO 2039-1

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Mold Shrinkage on Tensile Bar, flow	0.1 - 0.3	%	SABIC method
Density	1.61	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)	0.8	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.4	%	ISO 62
Melt Volume Rate, MVR at 360°C/5.0 kg	5	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Thermal Conductivity	0.33	W/m-°C	ISO 8302
CTE, 23°C to 150°C, flow	1.4E-05	1/°C	ISO 11359-2
CTE, 23°C to 150°C, xflow	4.5E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Vicat Softening Temp, Rate A/50	230	°C	ISO 306
Vicat Softening Temp, Rate B/50	217	°C	ISO 306
Vicat Softening Temp, Rate B/120	225	°C	ISO 306
*HDT/Be, 0.45MPa Edgew 120104 sp=100mm*	215	°C	ISO 75/Be
*HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm*	210	°C	ISO 75/Ae
Relative Temp Index, Elec	170	°C	UL 746B
Relative Temp Index, Mech w/impact	170	°C	UL 746B
Relative Temp Index, Mech w/o impact	170	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES