ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
Glass fiber, PTFE, and Graphite filled, standard flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 listing.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 0.84 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 160 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 64 | J/m | ASTM D256 |
Izod Impact, Reverse Notched, 3.2 mm | 170 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 135 | °C | |
Drying Time | 4 - 6 | Hrs | |
Drying Time (Cumulative) | 10 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 350 - 370 | °C | |
Nozzle Temperature | 350 - 370 | °C | |
Front - Zone 3 Temperature | 350 - 370 | °C | |
Middle - Zone 2 Temperature | 345 - 365 | °C | |
Rear - Zone 1 Temperature | 340 - 360 | °C | |
Mold Temperature | 135 - 165 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, brk, Type I, 5 mm/min | 82 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 1.2 | % | ASTM D638 |
Flexural Stress, yld, 2.6 mm/min, 100 mm span | 113 | MPa | ASTM D790 |
Flexural Stress, brk, 2.6 mm/min, 100 mm span | 137 | MPa | ASTM D790 |
Flexural Modulus, 2.6 mm/min, 100 mm span | 8820 | MPa | ASTM D790 |
Hardness, Rockwell M | 85 | - | ASTM D785 |
Taber Abrasion, CS-17, 1 kg | 33 | mg/1000cy | ASTM D1044 |
PV Limit, 0.51 m/s | 2.1 | MPa-m/s | SABIC method |
K-factor xE-10, PV=2000 psi-fpm vs Steel | 50 | - | SABIC method |
K-factor xE-10, PV=2000 psi-fpm vs Self | 1900 | - | SABIC method |
Coefficient of Friction on steel, Static | 0.25 | - | ASTM D1894 |
Coefficient of Friction on steel,Kinetic | 0.24 | - | ASTM D1894 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.67 | - | ASTM D792 |
Water Absorption, (23°C/24hrs) | 0.11 | % | ASTM D570 |
Mold Shrinkage, flow, 3.2 mm | 0.2 - 0.3 | % | SABIC method |
Melt Flow Rate, 337°C/6.6 kgf | 3.1 | g/10 min | ASTM D1238 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 233 | °C | ASTM D1525 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 212 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 1.62E-05 | 1/°C | ASTM E831 |
CTE, -20°C to 150°C, flow | 1.62E-05 | 1/°C | ASTM E831 |
Relative Temp Index, Elec | 105 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 0.84 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 160 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 64 | J/m | ASTM D256 |
Izod Impact, Reverse Notched, 3.2 mm | 170 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 135 | °C | |
Drying Time | 4 - 6 | Hrs | |
Drying Time (Cumulative) | 10 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 350 - 370 | °C | |
Nozzle Temperature | 350 - 370 | °C | |
Front - Zone 3 Temperature | 350 - 370 | °C | |
Middle - Zone 2 Temperature | 345 - 365 | °C | |
Rear - Zone 1 Temperature | 340 - 360 | °C | |
Mold Temperature | 135 - 165 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, brk, Type I, 5 mm/min | 82 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 1.2 | % | ASTM D638 |
Flexural Stress, yld, 2.6 mm/min, 100 mm span | 113 | MPa | ASTM D790 |
Flexural Stress, brk, 2.6 mm/min, 100 mm span | 137 | MPa | ASTM D790 |
Flexural Modulus, 2.6 mm/min, 100 mm span | 8820 | MPa | ASTM D790 |
Hardness, Rockwell M | 85 | - | ASTM D785 |
Taber Abrasion, CS-17, 1 kg | 33 | mg/1000cy | ASTM D1044 |
PV Limit, 0.51 m/s | 2.1 | MPa-m/s | SABIC method |
K-factor xE-10, PV=2000 psi-fpm vs Steel | 50 | - | SABIC method |
K-factor xE-10, PV=2000 psi-fpm vs Self | 1900 | - | SABIC method |
Coefficient of Friction on steel, Static | 0.25 | - | ASTM D1894 |
Coefficient of Friction on steel,Kinetic | 0.24 | - | ASTM D1894 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.67 | - | ASTM D792 |
Water Absorption, (23°C/24hrs) | 0.11 | % | ASTM D570 |
Mold Shrinkage, flow, 3.2 mm | 0.2 - 0.3 | % | SABIC method |
Melt Flow Rate, 337°C/6.6 kgf | 3.1 | g/10 min | ASTM D1238 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 233 | °C | ASTM D1525 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 212 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 1.62E-05 | 1/°C | ASTM E831 |
CTE, -20°C to 150°C, flow | 1.62E-05 | 1/°C | ASTM E831 |
Relative Temp Index, Elec | 105 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+15 | Ω.cm | IEC 60093 |
Surface Resistivity, ROA | >1.E+15 | Ω | IEC 60093 |
Relative Permittivity, 1 MHz | 6.2 | - | IEC 60250 |
Dissipation Factor, 50/60 Hz | 0.013 | - | IEC 60250 |
Dissipation Factor, 1 MHz | 0.022 | - | IEC 60250 |
Comparative Tracking Index | 200 | V | IEC 60112 |
Comparative Tracking Index, M | 100 | V | IEC 60112 |
Relative Permittivity, 50/60 Hz | 6.8 | - | IEC 60250 |
Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 0.84 | mm | UL 94 |
Glow Wire Flammability Index 960°C, passes at | 3.2 | mm | IEC 60695-2-12 |
Oxygen Index (LOI) | 48 | % | ISO 4589 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*4 -30°C | 15 | kJ/m² | ISO 180/1U |
Charpy Impact, notched, 23°C | 8 | kJ/m² | ISO 179/2C |
Charpy Impact, notched, -30°C | 8 | kJ/m² | ISO 179/2C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 150 | °C | |
Drying Time | 4 - 6 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 370 - 415 | °C | |
Nozzle Temperature | 360 - 405 | °C | |
Front - Zone 3 Temperature | 370 - 415 | °C | |
Middle - Zone 2 Temperature | 360 - 405 | °C | |
Rear - Zone 1 Temperature | 350 - 395 | °C | |
Hopper Temperature | 80 - 120 | °C | |
Mold Temperature | 140 - 180 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Taber Abrasion, CS-17, 1 kg | 30 | mg/1000cy | SABIC method |
PV Limit, 0.51 m/s | 2.1 | MPa-m/s | SABIC method |
K-factor xE-10, PV=2000 psi-fpm vs Steel | 50 | - | SABIC method |
K-factor xE-10, PV=2000 psi-fpm vs Self | 1900 | - | SABIC method |
Tensile Stress, break, 5 mm/min | 90 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 1 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 9900 | MPa | ISO 527 |
Flexural Stress, break, 2 mm/min | 120 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 7000 | MPa | ISO 178 |
Ball Indentation Hardness, H358/30 | 140 | MPa | ISO 2039-1 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage on Tensile Bar, flow | 0.1 - 0.3 | % | SABIC method |
Density | 1.68 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 0.7 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.3 | % | ISO 62 |
Melt Volume Rate, MVR at 360°C/5.0 kg | 5 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Thermal Conductivity | 0.43 | W/m-°C | ISO 8302 |
CTE, 23°C to 150°C, flow | 1.5E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate A/50 | 225 | °C | ISO 306 |
Vicat Softening Temp, Rate B/50 | 215 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 220 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Be |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 205 | °C | ISO 75/Ae |
Relative Temp Index, Elec | 105 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |