FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Oxygen Index (LOI) | 44 | % | ASTM D2863 |
Transparent, high flow Polyetherimide (Tg 217C). ECO Conforming. Improved processability for Fiber extrusion.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Oxygen Index (LOI) | 44 | % | ASTM D2863 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 1335 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 32 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 35 | J/m | ASTM D256 |
Izod Impact, Reverse Notched, 3.2 mm | 1175 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 33 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 150 | °C | |
Drying Time | 4 - 6 | Hrs | |
Drying Time (Cumulative) | 24 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 350 - 400 | °C | |
Nozzle Temperature | 345 - 400 | °C | |
Front - Zone 3 Temperature | 345 - 400 | °C | |
Middle - Zone 2 Temperature | 340 - 400 | °C | |
Rear - Zone 1 Temperature | 330 - 400 | °C | |
Mold Temperature | 135 - 165 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 5 mm/min | 110 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 105 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 7 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 60 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 3590 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 165 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 3520 | MPa | ASTM D790 |
Tensile Stress, yield, 5 mm/min | 105 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 85 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 6 | % | ISO 527 |
Tensile Strain, break, 5 mm/min | 60 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 3200 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 160 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 3300 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.27 | - | ASTM D792 |
Mold Shrinkage on Tensile Bar, flow | 0.5 - 0.7 | % | SABIC method |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate, 337°C/6.6 kgf | 17.8 | g/10 min | ASTM D1238 |
Density | 1.27 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 1.25 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.7 | % | ISO 62 |
Melt Volume Rate, MVR at 360°C/5.0 kg | 25 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 219 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 205 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 197 | °C | ASTM D648 |
HDT, 0.45 MPa, 6.4 mm, unannealed | 207 | °C | ASTM D648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 199 | °C | ASTM D648 |
CTE, -40°C to 150°C, flow | 5.5E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 150°C, xflow | 5.5E-05 | 1/°C | ASTM E831 |
CTE, 23°C to 150°C, flow | 5.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | Passes | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate A/50 | 215 | °C | ISO 306 |
Vicat Softening Temp, Rate B/50 | 211 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 212 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 200 | °C | ISO 75/Be |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Ae |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 193 | °C | ISO 75/Af |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 1.E+17 | Ω.cm | ASTM D257 |
Dielectric Strength, in air, 1.6 mm | 32.7 | kV/mm | ASTM D149 |
Dielectric Strength, in oil, 1.6 mm | 28 | kV/mm | ASTM D149 |
Relative Permittivity, 1 kHz | 3.15 | - | ASTM D150 |
Dissipation Factor, 1 kHz | 0.0013 | - | ASTM D150 |
Dissipation Factor, 2450 MHz | 0.0025 | - | ASTM D150 |
Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D495 |
Hot Wire Ignition {PLC) | 1 | PLC Code | UL 746A |
High Voltage Arc Track Rate {PLC} | 2 | PLC Code | UL 746A |
High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A |
Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Oxygen Index (LOI) | 44 | % | ASTM D2863 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 1335 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 32 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 35 | J/m | ASTM D256 |
Izod Impact, Reverse Notched, 3.2 mm | 1175 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 33 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 150 | °C | |
Drying Time | 4 - 6 | Hrs | |
Drying Time (Cumulative) | 24 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 350 - 400 | °C | |
Nozzle Temperature | 345 - 400 | °C | |
Front - Zone 3 Temperature | 345 - 400 | °C | |
Middle - Zone 2 Temperature | 340 - 400 | °C | |
Rear - Zone 1 Temperature | 330 - 400 | °C | |
Mold Temperature | 135 - 165 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 5 mm/min | 110 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 105 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 7 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 60 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 3590 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 165 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 3520 | MPa | ASTM D790 |
Tensile Stress, yield, 5 mm/min | 105 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 85 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 6 | % | ISO 527 |
Tensile Strain, break, 5 mm/min | 60 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 3200 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 160 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 3300 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.27 | - | ASTM D792 |
Mold Shrinkage on Tensile Bar, flow | 0.5 - 0.7 | % | SABIC method |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate, 337°C/6.6 kgf | 17.8 | g/10 min | ASTM D1238 |
Density | 1.27 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 1.25 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.7 | % | ISO 62 |
Melt Volume Rate, MVR at 360°C/5.0 kg | 25 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 219 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 205 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 197 | °C | ASTM D648 |
HDT, 0.45 MPa, 6.4 mm, unannealed | 207 | °C | ASTM D648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 199 | °C | ASTM D648 |
CTE, -40°C to 150°C, flow | 5.5E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 150°C, xflow | 5.5E-05 | 1/°C | ASTM E831 |
CTE, 23°C to 150°C, flow | 5.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | Passes | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate A/50 | 215 | °C | ISO 306 |
Vicat Softening Temp, Rate B/50 | 211 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 212 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 200 | °C | ISO 75/Be |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Ae |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 193 | °C | ISO 75/Af |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Oxygen Index (LOI) | 44 | % | ASTM D2863 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 1335 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 32 | J/m | ASTM D256 |
Izod Impact, notched, -30°C | 35 | J/m | ASTM D256 |
Izod Impact, Reverse Notched, 3.2 mm | 1175 | J/m | ASTM D256 |
Instrumented Dart Impact Total Energy, 23°C | 33 | J | ASTM D3763 |
Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 3 | kJ/m² | ISO 179/1eA |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 150 | °C | |
Drying Time | 4 - 6 | Hrs | |
Drying Time (Cumulative) | 24 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 350 - 400 | °C | |
Nozzle Temperature | 345 - 400 | °C | |
Front - Zone 3 Temperature | 345 - 400 | °C | |
Middle - Zone 2 Temperature | 340 - 400 | °C | |
Rear - Zone 1 Temperature | 330 - 400 | °C | |
Mold Temperature | 135 - 165 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 5 mm/min | 110 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 105 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min | 7 | % | ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min | 60 | % | ASTM D638 |
Tensile Modulus, 5 mm/min | 3590 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 165 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 3520 | MPa | ASTM D790 |
Tensile Stress, yield, 5 mm/min | 105 | MPa | ISO 527 |
Tensile Stress, break, 5 mm/min | 85 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 6 | % | ISO 527 |
Tensile Strain, break, 5 mm/min | 60 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 3200 | MPa | ISO 527 |
Flexural Stress, yield, 2 mm/min | 160 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 3300 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.27 | - | ASTM D792 |
Mold Shrinkage on Tensile Bar, flow | 0.5 - 0.7 | % | SABIC method |
Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
Melt Flow Rate, 337°C/6.6 kgf | 17.8 | g/10 min | ASTM D1238 |
Density | 1.27 | g/cm³ | ISO 1183 |
Water Absorption, (23°C/saturated) | 1.25 | % | ISO 62-1 |
Moisture Absorption (23°C / 50% RH) | 0.7 | % | ISO 62 |
Melt Volume Rate, MVR at 360°C/5.0 kg | 25 | cm³/10 min | ISO 1133 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Vicat Softening Temp, Rate B/50 | 219 | °C | ASTM D1525 |
HDT, 0.45 MPa, 3.2 mm, unannealed | 205 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 197 | °C | ASTM D648 |
HDT, 0.45 MPa, 6.4 mm, unannealed | 207 | °C | ASTM D648 |
HDT, 1.82 MPa, 6.4 mm, unannealed | 199 | °C | ASTM D648 |
CTE, -40°C to 150°C, flow | 5.5E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 150°C, xflow | 5.5E-05 | 1/°C | ASTM E831 |
CTE, 23°C to 150°C, flow | 5.E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
Ball Pressure Test, 125°C +/- 2°C | Passes | - | IEC 60695-10-2 |
Vicat Softening Temp, Rate A/50 | 215 | °C | ISO 306 |
Vicat Softening Temp, Rate B/50 | 211 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 212 | °C | ISO 306 |
HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 200 | °C | ISO 75/Be |
HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Ae |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 193 | °C | ISO 75/Af |