FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | ≥1.5 | mm | UL 94 |
30% Milled glass filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing. ISCC+ certified renewable bio-based solutions are available for this grade via differentiated color nomenclature.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | ≥1.5 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 32 | J/m | ASTM D256 |
Izod Impact, Reverse Notched, 3.2 mm | 309 | J/m | ASTM D256 |
Izod Impact, notched 80*10*4 +23°C | 4.9 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 150 | °C | |
Drying Time | 4 - 6 | Hrs | |
Drying Time (Cumulative) | 24 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 350 - 400 | °C | |
Nozzle Temperature | 345 - 400 | °C | |
Front - Zone 3 Temperature | 345 - 400 | °C | |
Middle - Zone 2 Temperature | 340 - 400 | °C | |
Rear - Zone 1 Temperature | 330 - 400 | °C | |
Mold Temperature | 135 - 165 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm | |
Shot to Cylinder Size | 40 - 60 | % | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 108 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 4 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 5231 | MPa | ASTM D638 |
Flexural Strength, 1.3 mm/min, 50 mm span | 173.2 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 5313 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.51 | - | ASTM D792 |
Melt Flow Rate, 337°C/6.6 kgf | 10.1 | g/10 min | ASTM D1238 |
Water Absorption, (23°C/24hrs) | 0.18 | % | ASTM D570 |
Water Absorption, (23°C/Saturated) | 0.98 | % | ASTM D570 |
Mold Shrinkage, flow, 3.2 mm | 0.3 - 0.4 | % | SABIC method |
Mold Shrinkage, xflow, 3.2 mm | 0.45 - 0.55 | % | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 211 | °C | ASTM D648 |
CTE, -40°C to 150°C, flow | 2.3E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 150°C, xflow | 2.7E-05 | 1/°C | ISO 11359-2 |
Relative Temp Index, Elec | 170 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 170 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 170 | °C | UL 746B |