AUR210G6 is a 30% glass fiber filled grade based on ULTEM recycle.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 370 - 410 | °C | |
| Nozzle Temperature | 360 - 410 | °C | |
| Front - Zone 3 Temperature | 370 - 420 | °C | |
| Middle - Zone 2 Temperature | 360 - 410 | °C | |
| Rear - Zone 1 Temperature | 350 - 400 | °C | |
| Hopper Temperature | 80 - 120 | °C | |
| Mold Temperature | 140 - 180 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 120 | MPa | ISO 527 |
| Tensile Modulus, 1 mm/min | 7500 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 180 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6500 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.53 | g/cm³ | ISO 1183 |
| Mold Shrinkage on Tensile Bar, flow | 0.2 - 0.4 | % | SABIC method |
| Melt Volume Rate, MVR at 337°C/6.7 kg | 4.5 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 212 | °C | ISO 75/Be |