Sustainable Grade
High flow Polyetherimide (Tg 217C) with internal mold release.. Very low outgassing and plateout, for automotive lighting applications where highly metallized, reflective surfaces are required. Haze onset temperature of 204C (SABIC IP method).
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 370 - 410 | °C | |
| Nozzle Temperature | 350 - 405 | °C | |
| Front - Zone 3 Temperature | 360 - 415 | °C | |
| Middle - Zone 2 Temperature | 350 - 405 | °C | |
| Rear - Zone 1 Temperature | 340 - 395 | °C | |
| Hopper Temperature | 80 - 120 | °C | |
| Mold Temperature | 140 - 180 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Taber Abrasion, CS-17, 1 kg | 10 | mg/1000cy | SABIC method |
| Tensile Stress, yield, 50 mm/min | 105 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 85 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 6 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 60 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 3300 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 160 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 3300 | MPa | ISO 178 |
| Ball Indentation Hardness, H358/30 | 140 | MPa | ISO 2039-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.5 - 0.7 | % | SABIC method |
| Density | 1.27 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 1.25 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.7 | % | ISO 62 |
| Melt Volume Rate, MVR at 340°C/5.0 kg | 13 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Thermal Conductivity | 0.24 | W/m-°C | ISO 8302 |
| CTE, 23°C to 150°C, flow | 5.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 5.E-05 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate A/50 | 215 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 211 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 212 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 195 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 190 | °C | ISO 75/Ae |
| Metallized Haze Onset | 204 | °C | SABIC method |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.