Sustainable Grade
10% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming, UL94 V0 and 5 VA listing.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥3 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 1 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 3 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 4 | ≥3 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 3 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94-5VA Flame Class Rating | ≥1.5 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 37 | J/m | ASTM D256 |
| Izod Impact, Reverse Notched, 3.2 mm | 357 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Drying Time (Cumulative) | 24 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 365 - 390 | °C | |
| Nozzle Temperature | 360 - 380 | °C | |
| Front - Zone 3 Temperature | 365 - 390 | °C | |
| Middle - Zone 2 Temperature | 355 - 375 | °C | |
| Rear - Zone 1 Temperature | 345 - 365 | °C | |
| Mold Temperature | 135 - 165 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 117 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 112 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 4 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 4750 | MPa | ASTM D638 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 193 | MPa | ASTM D790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 4890 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.36 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.7 - 0.9 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 0.6 - 0.8 | % | SABIC method |
| Melt Flow Rate, 337°C/6.6 kgf | 6.9 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 6.4 mm, unannealed | 215 | °C | ASTM D648 |
| Relative Temp Index, Elec | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥3 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 1 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 3 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 4 | ≥3 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 3 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94-5VA Flame Class Rating | ≥1.5 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 37 | J/m | ASTM D256 |
| Izod Impact, Reverse Notched, 3.2 mm | 357 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Drying Time (Cumulative) | 24 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 365 - 390 | °C | |
| Nozzle Temperature | 360 - 380 | °C | |
| Front - Zone 3 Temperature | 365 - 390 | °C | |
| Middle - Zone 2 Temperature | 355 - 375 | °C | |
| Rear - Zone 1 Temperature | 345 - 365 | °C | |
| Mold Temperature | 135 - 165 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 117 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 112 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 4 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 4750 | MPa | ASTM D638 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 193 | MPa | ASTM D790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 4890 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.36 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.7 - 0.9 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 0.6 - 0.8 | % | SABIC method |
| Melt Flow Rate, 337°C/6.6 kgf | 6.9 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 6.4 mm, unannealed | 215 | °C | ASTM D648 |
| Relative Temp Index, Elec | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |