Sustainable Grade
20% Glass fiber filled, enhanced flow Polyetherimide copolymer (Tg 225C) with internal mold release and enhanced chemical resistance to strong acids, bases, aromatics, and ketones. ECO conforming.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 2 | ≥3 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 3 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 3 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 4 | ≥3 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94-5VA Flame Class Rating | ≥1.5 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 74 | J/m | ASTM D256 |
| Izod Impact, Reverse Notched, 3.2 mm | 459 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Drying Time (Cumulative) | 24 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 365 - 390 | °C | |
| Nozzle Temperature | 360 - 380 | °C | |
| Front - Zone 3 Temperature | 365 - 390 | °C | |
| Middle - Zone 2 Temperature | 355 - 375 | °C | |
| Rear - Zone 1 Temperature | 345 - 365 | °C | |
| Mold Temperature | 135 - 165 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 137 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 144 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 6890 | MPa | ASTM D638 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 213 | MPa | ASTM D790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 6890 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.45 | - | ASTM D792 |
| Melt Flow Rate, 337°C/6.6 kgf | 5.5 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 6.4 mm, unannealed | 218 | °C | ASTM D648 |
| Relative Temp Index, Elec | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 4 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 2 | ≥3 | mm | UL 746A |
| Hot-Wire Ignition (HWI), PLC 3 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 3 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 4 | ≥3 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94-5VA Flame Class Rating | ≥1.5 | mm | UL 94 |
| UL Recognized, 94V-0 Flame Class Rating | 1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 74 | J/m | ASTM D256 |
| Izod Impact, Reverse Notched, 3.2 mm | 459 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Drying Time (Cumulative) | 24 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 365 - 390 | °C | |
| Nozzle Temperature | 360 - 380 | °C | |
| Front - Zone 3 Temperature | 365 - 390 | °C | |
| Middle - Zone 2 Temperature | 355 - 375 | °C | |
| Rear - Zone 1 Temperature | 345 - 365 | °C | |
| Mold Temperature | 135 - 165 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Shot to Cylinder Size | 40 - 60 | % | |
| Vent Depth | 0.025 - 0.076 | mm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 5 mm/min | 137 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 5 mm/min | 144 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 6890 | MPa | ASTM D638 |
| Flexural Stress, yld, 2.6 mm/min, 100 mm span | 213 | MPa | ASTM D790 |
| Flexural Modulus, 2.6 mm/min, 100 mm span | 6890 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.45 | - | ASTM D792 |
| Melt Flow Rate, 337°C/6.6 kgf | 5.5 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 6.4 mm, unannealed | 218 | °C | ASTM D648 |
| Relative Temp Index, Elec | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |