FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | ≥0.8 | mm | UL 94 |
High flow high gloss polyetherimide (PEI) blend with internal mold release and enhanced ductility.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | ≥0.8 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 40 | J/m | ASTM D256 |
Izod Impact, unnotched, 23°C | 2097 | J/m | ASTM D4812 |
Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
Izod Impact, unnotched 80*10*4 +23°C | 128 | kJ/m² | ISO 180/1U |
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 3.3 | kJ/m² | ISO 179/1eA |
Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 86 | kJ/m² | ISO 179/1eU |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 135 - 150 | °C | |
Drying Time | 4 - 6 | Hrs | |
Drying Time (Cumulative) | 24 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 320 - 355 | °C | |
Nozzle Temperature | 325 - 350 | °C | |
Front - Zone 3 Temperature | 330 - 355 | °C | |
Middle - Zone 2 Temperature | 320 - 345 | °C | |
Rear - Zone 1 Temperature | 310 - 330 | °C | |
Mold Temperature | 110 - 165 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw Speed | 40 - 70 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 107 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 50 mm/min | 80 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 50 mm/min | 6.8 | % | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 25 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 3150 | MPa | ASTM D638 |
Flexural Strength, 1.3 mm/min, 50 mm span | 166 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 3190 | MPa | ASTM D790 |
Tensile Stress, yield, 50 mm/min | 108 | MPa | ISO 527 |
Tensile Stress, break, 50 mm/min | 80 | MPa | ISO 527 |
Tensile Strain, yield, 50 mm/min | 6.7 | % | ISO 527 |
Tensile Strain, break, 50 mm/min | 25 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 3090 | MPa | ISO 527 |
Flexural Strength, 2 mm/min | 156 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2950 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.285 | - | ASTM D792 |
Density | 1.285 | g/cm³ | ISO 1183 |
Moisture Absorption, (23°C/50% RH/24hrs) | 0.07 | % | ISO 62-4 |
Melt Flow Rate, 350°C/2.16 kgf | 24 | g/10 min | ASTM D1238 |
Melt Flow Rate, 337°C/6.7 kgf | 53 | g/10 min | ASTM D1238 |
Mold Shrinkage, flow | 0.58 | % | SABIC method |
Mold Shrinkage, xflow | 0.62 | % | SABIC method |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 182 | °C | ASTM D648 |
HDT, 1.82 MPa, 3.2mm, unannealed | 168 | °C | ASTM D648 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 181 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 168 | °C | ISO 75/Af |
CTE, 23°C to 150°C, flow | 5.5E-05 | 1/°C | ASTM E831 |
CTE, 23°C to 150°C, xflow | 5.8E-05 | 1/°C | ASTM E831 |
CTE, 23°C to 150°C, flow | 5.5E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 150°C, xflow | 5.8E-05 | 1/°C | ISO 11359-2 |
Vicat Softening Temp, Rate B/50 | 184 | °C | ASTM D1525 |
Vicat Softening Temp, Rate B/120 | 184 | °C | ASTM D1525 |
Vicat Softening Temp, Rate B/50 | 187 | °C | ISO 306 |
Vicat Softening Temp, Rate B/120 | 188 | °C | ISO 306 |
Relative Temp Index, Elec | 105 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.