Tensile Stress, yld, Type I, 5 mm/min |
110 |
MPa |
ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min |
90 |
MPa |
ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min |
7 |
% |
ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min |
60 |
% |
ASTM D638 |
Tensile Modulus, 5 mm/min |
3580 |
MPa |
ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span |
160 |
MPa |
ASTM D790 |
Flexural Stress, yld, 2.6 mm/min, 100 mm span |
165 |
MPa |
ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span |
3550 |
MPa |
ASTM D790 |
Flexural Modulus, 2.6 mm/min, 100 mm span |
3510 |
MPa |
ASTM D790 |
Taber Abrasion, CS-17, 1 kg |
10 |
mg/1000cy |
SABIC method |
Tensile Stress, yield, 50 mm/min |
105 |
MPa |
ISO 527 |
Tensile Stress, break, 50 mm/min |
85 |
MPa |
ISO 527 |
Tensile Strain, yield, 50 mm/min |
6 |
% |
ISO 527 |
Tensile Strain, break, 50 mm/min |
60 |
% |
ISO 527 |
Tensile Modulus, 1 mm/min |
3200 |
MPa |
ISO 527 |
Flexural Stress, yield, 2 mm/min |
160 |
MPa |
ISO 178 |
Flexural Modulus, 2 mm/min |
3300 |
MPa |
ISO 178 |
Ball Indentation Hardness, H358/30 |
140 |
MPa |
ISO 2039-1 |