40% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Specific grade-colors are designed and certified for use in Potable Water applications. KTW, WRAS, ACS, NSF-61 and W270 certified. US FDA and European Food Contact approved.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Comparative Tracking Index (UL) {PLC} | 5 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥1.5 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 4 | ≥1.5 | mm | UL 746A |
| High Voltage Arc Track Rate {PLC} | 4 | PLC Code | UL 746A |
| Arc Resistance, Tungsten {PLC} | 5 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | ≥0.25 | mm | UL 94 |
| Glow Wire Ignitability Temperature, 1.5 mm | 875 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 1.0 mm | 850 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index, 1.5 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 1.0 mm | 960 | °C | IEC 60695-2-12 |
| Oxygen Index (LOI) | 48 | % | ISO 4589 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 35 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 35 | kJ/m² | ISO 180/1U |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 40 | kJ/m² | ISO 179/1eU |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 370 - 410 | °C | |
| Nozzle Temperature | 370 - 410 | °C | |
| Front - Zone 3 Temperature | 380 - 420 | °C | |
| Middle - Zone 2 Temperature | 370 - 410 | °C | |
| Rear - Zone 1 Temperature | 350 - 390 | °C | |
| Hopper Temperature | 80 - 100 | °C | |
| Mold Temperature | 140 - 180 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Taber Abrasion, CS-17, 1 kg | 20 | mg/1000cy | SABIC method |
| Tensile Stress, break, 5 mm/min | 180 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 11500 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 240 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 10000 | MPa | ISO 178 |
| Ball Indentation Hardness, H358/30 | 170 | MPa | ISO 2039-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.1 - 0.3 | % | SABIC method |
| Density | 1.61 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.8 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.4 | % | ISO 62 |
| Melt Volume Rate, MVR at 360°C/5.0 kg | 5 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Thermal Conductivity | 0.33 | W/m-°C | ISO 8302 |
| CTE, 23°C to 150°C, flow | 1.4E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 150°C, xflow | 4.5E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 230 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 217 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 225 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 215 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 210 | °C | ISO 75/Ae |
| Relative Temp Index, Elec | 170 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 170 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 170 | °C | UL 746B |