Tensile Stress, yld, Type I, 5 mm/min |
75 |
MPa |
ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min |
75 |
MPa |
ASTM D638 |
Tensile Strain, yld, Type I, 5 mm/min |
2 |
% |
ASTM D638 |
Tensile Strain, brk, Type I, 5 mm/min |
2 |
% |
ASTM D638 |
Tensile Modulus, 5 mm/min |
7200 |
MPa |
ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span |
110 |
MPa |
ASTM D790 |
Flexural Stress, brk, 1.3 mm/min, 50 mm span |
110 |
MPa |
ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span |
6000 |
MPa |
ASTM D790 |
Tensile Stress, yield, 5 mm/min |
75 |
MPa |
ISO 527 |
Tensile Stress, break, 5 mm/min |
75 |
MPa |
ISO 527 |
Tensile Strain, yield, 5 mm/min |
2 |
% |
ISO 527 |
Tensile Strain, break, 5 mm/min |
2 |
% |
ISO 527 |
Tensile Modulus, 1 mm/min |
7400 |
MPa |
ISO 527 |
Flexural Stress, yield, 2 mm/min |
125 |
MPa |
ISO 178 |
Flexural Stress, break, 2 mm/min |
125 |
MPa |
ISO 178 |
Flexural Strain, break, 2 mm/min |
3 |
% |
ISO 178 |
Flexural Modulus, 2 mm/min |
6300 |
MPa |
ISO 178 |
Ball Indentation Hardness, H358/30 |
142 |
MPa |
ISO 2039-1 |
Hardness, Rockwell R |
120 |
- |
ISO 2039-2 |