ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 9.E+12 | Ω | ASTM D257 |
VALOX SLWM2105 resin is based on Polycarbonate / Polyester blend containing proprietary fillers. Added features of this grade include: Permanently Anti-Static.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 9.E+12 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched, 23°C | 41 | J/m | ASTM D256 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 110 | °C | |
Drying Time | 3 - 5 | Hrs | |
Melt Temperature | 230 - 260 | °C | |
Nozzle Temperature | 240 - 260 | °C | |
Front - Zone 3 Temperature | 240 - 260 | °C | |
Middle - Zone 2 Temperature | 230 - 250 | °C | |
Rear - Zone 1 Temperature | 220 - 240 | °C | |
Mold Temperature | 30 - 60 | °C |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yld, Type I, 50 mm/min | 46 | MPa | ASTM D638 |
Tensile Stress, brk, Type I, 5 mm/min | 46 | MPa | ASTM D638 |
Tensile Strain, yld, Type I, 10 mm/min | 20 | % | SABIC - Japan Method |
Tensile Strain, brk, Type I, 10 mm/min | 20 | % | SABIC - Japan Method |
Tensile Modulus, 5 mm/min | 2420 | MPa | ASTM D638 |
Flexural Stress, yld, 1.3 mm/min, 50 mm span | 77 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 2300 | MPa | ASTM D790 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.32 | - | ASTM D792 |
Mold Shrinkage, flow, 3.2 mm | 1.5 - 1.8 | % | SABIC method |
Melt Flow Rate, 250°C/1.2 kgf | 30 | g/10 min | ASTM D1238 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 0.45 MPa, 3.2 mm, unannealed | 161 | °C | ASTM D648 |