ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 7.1E+15 | Ω.cm | ASTM D257 |
Comparative Tracking Index | 600 | V | IEC 60112 |
Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
FLEX NORYL WCA955 resin is a flexible, non-reinforced injection moldable blend of Polyphenylene Ether (PPE) + Styrene Ethylene Butylene Styrene (SEBS) + Polyolefin. This material contains non-halogenated flame retardant and carries a UL94 flame rating of V0 at 6mm. FLEX NORYL WCA955 resin is intended for evaluation in over-molding applications such as plugs, strain reliefs, and connectors. It has a Shore A Hardness reading of 84 and exhibits low specific gravity, very low water absorption, and dimensional stability.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 7.1E+15 | Ω.cm | ASTM D257 |
Comparative Tracking Index | 600 | V | IEC 60112 |
Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥0.6 | mm | UL 94 |
UL Recognized, 94V-0 Flame Class Rating | 6 | mm | UL 94 |
Glow Wire Flammability Index 750°C, passes at | 3 | mm | IEC 60695-2-12 |
Glow Wire Ignitability Temperature, 3.0 mm | 750 | °C | IEC 60695-2-13 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Brittleness Temperature | <-40 | °C | ASTM D746 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 60 - 80 | °C | |
Drying Time | 4 - 6 | Hrs | |
Drying Time (Cumulative) | 8 | Hrs | |
Maximum Moisture Content | 0.01 | % | |
Melt Temperature | 220 - 250 | °C | |
Nozzle Temperature | 220 - 250 | °C | |
Front - Zone 3 Temperature | 220 - 250 | °C | |
Middle - Zone 2 Temperature | 210 - 240 | °C | |
Rear - Zone 1 Temperature | 180 - 220 | °C | |
Mold Temperature | 40 - 60 | °C | |
Back Pressure | 3 - 10 | MPa | |
Screw Speed | 30 - 80 | rpm | |
Shot to Cylinder Size | 30 - 70 | % | |
Vent Depth | 0.03 - 0.05 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, brk, Type I, 50 mm/min | 6 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 150 | % | ASTM D638 |
Flexural Modulus, 12.5 mm/min, 100 mm span | 50 | MPa | ASTM D790 |
Hardness, Shore A, 30S reading | 84 | - | ASTM D2240 |
Tensile Stress, break, 50 mm/min | 7 | MPa | ISO 527 |
Tensile Strain, break, 50 mm/min | 175 | % | ISO 527 |
Flexural Modulus, 12.5 mm/min | 50 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.01 | - | ASTM D792 |
Mold Shrinkage, flow, 24 hrs | 0.95 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.75 | % | ASTM D955 |
Melt Flow Rate, 210°C/5 kgf | 24 | g/10 min | ASTM D1238 |
Melt Flow Rate, 250°C/2.16 kgf | 27 | g/10 min | ASTM D1238 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Volume Resistivity | 7.1E+15 | Ω.cm | ASTM D257 |
Comparative Tracking Index | 600 | V | IEC 60112 |
Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94HB Flame Class Rating | ≥0.6 | mm | UL 94 |
UL Recognized, 94V-0 Flame Class Rating | 6 | mm | UL 94 |
Glow Wire Flammability Index 750°C, passes at | 3 | mm | IEC 60695-2-12 |
Glow Wire Ignitability Temperature, 3.0 mm | 750 | °C | IEC 60695-2-13 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Brittleness Temperature | <-40 | °C | ASTM D746 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 60 - 80 | °C | |
Drying Time | 4 - 6 | Hrs | |
Drying Time (Cumulative) | 8 | Hrs | |
Maximum Moisture Content | 0.01 | % | |
Melt Temperature | 220 - 250 | °C | |
Nozzle Temperature | 220 - 250 | °C | |
Front - Zone 3 Temperature | 220 - 250 | °C | |
Middle - Zone 2 Temperature | 210 - 240 | °C | |
Rear - Zone 1 Temperature | 180 - 220 | °C | |
Mold Temperature | 40 - 60 | °C | |
Back Pressure | 3 - 10 | MPa | |
Screw Speed | 30 - 80 | rpm | |
Shot to Cylinder Size | 30 - 70 | % | |
Vent Depth | 0.03 - 0.05 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, brk, Type I, 50 mm/min | 6 | MPa | ASTM D638 |
Tensile Strain, brk, Type I, 50 mm/min | 150 | % | ASTM D638 |
Flexural Modulus, 12.5 mm/min, 100 mm span | 50 | MPa | ASTM D790 |
Hardness, Shore A, 30S reading | 84 | - | ASTM D2240 |
Tensile Stress, break, 50 mm/min | 7 | MPa | ISO 527 |
Tensile Strain, break, 50 mm/min | 175 | % | ISO 527 |
Flexural Modulus, 12.5 mm/min | 50 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Specific Gravity | 1.01 | - | ASTM D792 |
Mold Shrinkage, flow, 24 hrs | 0.95 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.75 | % | ASTM D955 |
Melt Flow Rate, 210°C/5 kgf | 24 | g/10 min | ASTM D1238 |
Melt Flow Rate, 250°C/2.16 kgf | 27 | g/10 min | ASTM D1238 |