LNP™ ELCRIN™ EXL1213TB

Sustainable Grade

ELCRIN EXL1213TB polycarbonate (PC) siloxane copolymer is transparent injection molding grade with major component synthesized from Bio source. This grade offers extreme low temperature ductility in combination with high flow characteristics, excellent processability and good chemical resistance. It is a general purpose product available in transparent and opaque colors and is an excellent candidate for a broad range of applications

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
Amorphous
Chemical Resistance
Good Processability
High temperature resistance
Impact resistant
Low temperature impact
No PFAS intentionally added
Sustainable (bio-based offerings)
Transparent/Translucent

Industry

Material previously used in

Applications

Possible usage of material

Displays
Electronic Components
Electronics

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	≥0.70	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	830	J/m	ASTM D256
Izod Impact, notched, -30°C	620	J/m	ASTM D256
*Izod Impact, notched 80103 +23°C*	53	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 -30°C*	19	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80103 +23°C*	132	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80103 -30°C*	133	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80103 sp=62mm*	53	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80103 sp=62mm*	21	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80103 sp=62mm*	94	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80103 sp=62mm*	95	kJ/m²	ISO 179/1eU
Instrumented Dart Impact Total Energy, 23°C	68	J	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	3 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	290 - 320	°C
Nozzle Temperature	290 - 310	°C
Front - Zone 3 Temperature	295 - 320	°C
Middle - Zone 2 Temperature	285 - 305	°C
Rear - Zone 1 Temperature	280 - 295	°C
Mold Temperature	80 - 115	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	40 - 70	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yld, Type I, 50 mm/min	56	MPa	ASTM D638
Tensile Stress, brk, Type I, 50 mm/min	53	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5.8	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	90	%	ASTM D638
Tensile Modulus, 50 mm/min	2060	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	91	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	2080	MPa	ASTM D790
Tensile Stress, yield, 50 mm/min	56	MPa	ISO 527
Tensile Stress, break, 50 mm/min	56	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Tensile Strain, break, 50 mm/min	80	%	ISO 527
Tensile Modulus, 1 mm/min	2076	MPa	ISO 527
Flexural Strength, 2 mm/min	86	MPa	ISO 178
Flexural Modulus, 2 mm/min	1950	MPa	ISO 178

OPTICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Light Transmission at 2.0 mm	89	%	SABIC method
Haze, 2mm	1.0	%	SABIC method

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.18	-	ASTM D792
Density	1.18	g/cm³	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.05	%	ISO 62
Melt Flow Rate, 300°C/1.2 kgf	14.7	g/10 min	ASTM D1238
Melt Volume Rate, MVR at 300°C/1.2 kg	13.3	cm³/10 min	ISO 1133
Mold Shrinkage, flow, 3.2 mm	0.4 - 0.8	%	SABIC method
Mold Shrinkage, xflow, 3.2 mm	0.4 - 0.8	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	119	°C	ASTM D648
*HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm*	121	°C	ISO 75/Ae
CTE, -40°C to 40°C, flow	8.4E-5	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	9E-5	1/°C	ASTM E831
CTE, 23°C to 80°C, flow	9.7E-5	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	9.2E-5	1/°C	ISO 11359-2
Vicat Softening Temp, Rate B/50	147	°C	ASTM D1525
Vicat Softening Temp, Rate B/50	140	°C	ISO 306
Vicat Softening Temp, Rate B/120	141	°C	ISO 306
Ball Pressure Test, 125°C +/- 2°C	Pass	-	IEC 60695-10-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES