LNP KONDUIT OX11314 compound is based on Polyphenylene Sulfide (PPS) resin containing mineral and glass fiber. Added features of this grade include: Thermally Conductive, Electrically Insulative and Non-Brominated, Non-Chlorinated Flame Retardant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | >1.E+15 | Ω | ASTM D257 |
| Dielectric Strength, in oil, 1.0 mm | >4 | kV/mm | ASTM D149 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Comparative Tracking Index (UL) {PLC} | 0 | PLC Code | UL 746A |
| Hot-Wire Ignition (HWI), PLC 0 | ≥0.8 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 0 | ≥1 | mm | UL 746A |
| High Amp Arc Ignition (HAI), PLC 1 | ≥0.8 | mm | UL 746A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94V-0 Flame Class Rating | ≥0.8 | mm | UL 94 |
| Glow Wire Ignitability Temperature, 1.0 mm | 875 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 3.0 mm | 960 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index, 3.0 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 1.0 mm | 960 | °C | IEC 60695-2-12 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Charpy Impact, unnotched, 23°C | 5 | kJ/m² | ISO 179/2C |
| Izod Impact, unnotched, 23°C | 90 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 25 | J/m | ASTM D256 |
| Charpy Impact, notched, 23°C | 2 | kJ/m² | ISO 179/2C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 320 - 350 | °C | |
| Front - Zone 3 Temperature | 315 - 345 | °C | |
| Middle - Zone 2 Temperature | 315 - 345 | °C | |
| Rear - Zone 1 Temperature | 315 - 345 | °C | |
| Mold Temperature | 110 - 150 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 60 - 100 | rpm | |
| Shot to Cylinder Size | 50 - 75 | % |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 44 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 0.6 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 12160 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 47 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 11200 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.9 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.18 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.24 | % | ASTM D955 |
| Water Absorption, 23°C/24hrs | 0.1 | % | SABIC method |
| Moisture Absorption (23°C / 50% RH) | 0.03 | % | ISO 62 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 6.4 mm, unannealed | 191 | °C | ASTM D648 |
| CTE, 40°C to 120°C, flow | 2.6E-05 | 1/°C | ASTM E831 |
| CTE, 40°C to 120°C, xflow | 5.1E-05 | 1/°C | ASTM E831 |
| Specific Heat | 1.44 | J/g-°C | ASTM C351 |
| Thermal Conductivity through-plane, 10*10*3mm sample | 1 | W/m-K | ASTM E1461-07 |
| Thermal Conductivity in-plane, 25*0.4mm disc | 2.1 | W/m-K | ASTM E1461-07 |
| Thermal Conductivity through-plane, ?80*3mm discs | 0.9 | W/m-K | ISO 22007-2 |
| Thermal Conductivity in-plane, ?80*3mm discs | 2.22 | W/m-K | ISO 22007-2 |
| Relative Temp Index, Elec | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 130 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+15 | Ω | ASTM D257 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 2 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 - 150 | °C | |
| Drying Time | 4 | Hrs | |
| Melt Temperature | 320 - 350 | °C | |
| Front - Zone 3 Temperature | 315 - 345 | °C | |
| Middle - Zone 2 Temperature | 315 - 345 | °C | |
| Rear - Zone 1 Temperature | 315 - 345 | °C | |
| Mold Temperature | 110 - 150 | °C | |
| Back Pressure | 0.3 - 0.7 | MPa | |
| Screw Speed | 60 - 100 | rpm | |
| Shot to Cylinder Size | 50 - 75 | % |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 50 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 0.5 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 15000 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 75 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 15500 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.26 | % | SABIC method |
| Mold Shrinkage, flow, 24 hrs | 0.39 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.41 | % | ISO 294 |
| Density | 1.91 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, -40°C to 40°C, flow | 2.E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 3.E-05 | 1/°C | ASTM E831 |
| CTE, -30°C to 80°C, flow | 2.1E-05 | 1/°C | ISO 11359-2 |
| CTE, -30°C to 80°C, xflow | 3.2E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, flow | 2.2E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 3.5E-05 | 1/°C | ISO 11359-2 |
| Thermal Conductivity through-plane, ?80*3mm discs | 0.75 | W/m-K | ISO 22007-2 |
| Thermal Conductivity in-plane, ?80*3mm discs | 1.95 | W/m-K | ISO 22007-2 |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Vicat Softening Temp, Rate B/120 | 254 | °C | ISO 306 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 261 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 211 | °C | ISO 75/Af |