LNP LUBRICOMP AL002 compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing 10% PTFE. Added features of this grade include Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 843 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 42 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 - 0.1 | % | |
| Melt Temperature | 260 | °C | |
| Front - Zone 3 Temperature | 265 - 275 | °C | |
| Middle - Zone 2 Temperature | 230 - 245 | °C | |
| Rear - Zone 1 Temperature | 205 - 215 | °C | |
| Mold Temperature | 70 - 80 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 37 | MPa | ASTM D638 |
| Tensile Stress, break | 32 | MPa | ASTM D638 |
| Tensile Strain, yield | 2.6 | % | ASTM D638 |
| Tensile Strain, break | 21 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2130 | MPa | ASTM D638 |
| Flexural Stress | 62 | MPa | ASTM D790 |
| Flexural Modulus | 2190 | MPa | ASTM D790 |
| Tensile Stress, yield | 37 | MPa | ISO 527 |
| Tensile Stress, break | 32 | MPa | ISO 527 |
| Tensile Strain, yield | 2.2 | % | ISO 527 |
| Tensile Strain, break | 32.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1940 | MPa | ISO 527 |
| Flexural Stress | 63 | MPa | ISO 178 |
| Flexural Modulus | 2200 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.1 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.5 - 0.7 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.5 - 0.7 | % | ASTM D955 |
| Mold Shrinkage, flow, 24 hrs | 0.5 - 0.7 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 0.5 - 0.7 | % | ISO 294 |
| Density | 1.11 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 91 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 89 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 9.54E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 9.54E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 9.6E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 9.5E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 92 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 84 | °C | ISO 75/Af |