FLAME CHARACTERISTICS
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-1 Flame Class Rating | ≥3 | mm | UL 94 |
LNP LUBRICOMP DP002 compound is based on Polycarbonate (PC) resin containing 10% PTFE/silicone. Added features of this grade include: Internally Lubricated, Wear Resistant, Easy Molding,
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-1 Flame Class Rating | ≥3 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, notched 80*10*4 +23°C | 16 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 4 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 300 - 315 | °C | |
Front - Zone 3 Temperature | 310 - 320 | °C | |
Middle - Zone 2 Temperature | 305 - 315 | °C | |
Rear - Zone 1 Temperature | 295 - 305 | °C | |
Mold Temperature | 80 - 110 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, yield, 5 mm/min | 53 | MPa | ISO 527 |
Tensile Strain, yield, 5 mm/min | 24.3 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 2100 | MPa | ISO 527 |
Flexural Stress, break, 2 mm/min | 72 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 2100 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.23 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
CTE, 23°C to 60°C, flow | 7.2E-05 | 1/°C | ISO 11359-2 |
CTE, 23°C to 60°C, xflow | 7.4E-05 | 1/°C | ISO 11359-2 |
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 136 | °C | ISO 75/Bf |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 125 | °C | ISO 75/Af |