LNP™ LUBRILOY™ Compound D2000I

LNP LUBRILOY D2000I compound is based on Polycarbonate (PC) resin containing proprietary lubricant. Added features of this grade include: Wear Resistant, High Impact.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Impact resistant
No PFAS intentionally added
Wear resistant

Industry

Material previously used in

Building Component
Commercial Appliance
Electrical
Home Appliances
Mobile Phone - Computer - Tablets
Personal Accessory
Sport/Leisure

Applications

Possible usage of material

Document Handling
Head Protection
Lab Ware and Clinical Diagnostics
Wireless Communications

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Yellow Card Link 2	View	-	-
UL Recognized, 94HB Flame Class Rating	1.2	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, unnotched, 23°C	1762	J/m	ASTM D4812
Izod Impact, notched, 23°C	779	J/m	ASTM D256
Izod Impact, notched, -40°C	542	J/m	ASTM D256
*Izod Impact, notched 80104 -40°C*	43	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	100	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	290 - 315	°C
Front - Zone 3 Temperature	280 - 310	°C
Middle - Zone 2 Temperature	280 - 300	°C
Rear - Zone 1 Temperature	275 - 300	°C
Mold Temperature	65 - 95	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, yield	49	MPa	ASTM D638
Tensile Stress, break	54	MPa	ASTM D638
Tensile Strain, yield	5.6	%	ASTM D638
Tensile Strain, break	130	%	ASTM D638
Flexural Stress	68	MPa	ASTM D790
Flexural Modulus	1860	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.17	g/cm³	ASTM D792
Wear Factor Washer	35	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Dynamic COF	0.32	-	ASTM D3702 Modified: Manual
Static COF	0.22	-	ASTM D3702 Modified: Manual

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	120	°C	ASTM D648
CTE, -40°C to 40°C, flow	1.31E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	1.35E-04	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	8.01E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	8.54E-05	1/°C	ISO 11359-2
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

CAE Cards

Please login to view graphs, download multi-point data or literature

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES