LNP™ LUBRILOY™ Compound N2000

LNP LUBRILOY N2000 compound is based on unfilled Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS). Added features of this grade include excellent BSR (Buzz, Squeak, Rattle) performance. Custom colorable, low gloss, internally lubricated without silicones or fluorinated polymers. Good impact and flow properties.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate + ABS (PC+ABS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Impact resistant
No PFAS intentionally added
Wear resistant

Industry

Material previously used in

Automotive Interiors
Commercial Appliance
Home Appliances
Mobile Phone - Computer - Tablets
Sport/Leisure

Applications

Possible usage of material

Amusement Machine
ATM/Ticket Machine
Audio
Auto Aftermarket
Console
Display
Document Handling
Enclosure/Housing/Cover
Enclosures
Glove Box
Infotainment/Telematic
Infrastructure
Trim
infotainment bezel
automotive interior bezel
bsr
buzz
squeak
rattle
door panel
trim panel
non-ptfe
no ptfe
ptfe free
pfas free
pfoa free
automotive interior
car navigation
door trim
back mirror
non ptfe
pfoa
pfas

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	37	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	16	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	31	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	16	kJ/m²	ISO 179/1eA
Izod Impact, notched, 23°C	39	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80 - 110	°C
Drying Time	3 - 4	Hrs
Maximum Moisture Content	0.012 - 0.02	%
Melt Temperature	240 - 265	°C
Rear - Zone 1 Temperature	240 - 265	°C
Middle - Zone 2 Temperature	240 - 265	°C
Front - Zone 3 Temperature	240 - 265	°C
Nozzle Temperature	240 - 265	°C
Mold Temperature	60 - 90	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	20 - 100	rpm
Vent Depth	0.038 - 0.051	mm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	2058	MPa	ISO 527
Tensile Stress, yield, 50 mm/min	46	MPa	ISO 527
Tensile Stress, break, 50 mm/min	42	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5	%	ISO 527
Flexural Modulus, 2 mm/min	2016	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.11	g/cm³	ISO 1183
Dynamic COF	0.37	-	ASTM D3702 Modified: Manual
Wear Factor Washer	85	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Specific Gravity	1.12	-	ASTM D792
Water Absorption, (23°C/24hrs)	0.12	%	ASTM D570
Mold Shrinkage, flow	0.4 - 0.6	%	SABIC method
Mold Shrinkage, xflow	0.4 - 0.6	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 1.82 MPa, 3.2mm, unannealed	102	°C	ASTM D648

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES