LNP LUBRILOY R2000 compound is based on Nylon 6/6 resin containing proprietary lubricant. Added features of this grade include: Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 141 | kJ/m² | ISO 180/1U |
| Izod Impact, notched, 23°C | 62 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 1724 | J/m | ASTM D4812 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.15 - 0.25 | % | |
| Melt Temperature | 270 - 280 | °C | |
| Front - Zone 3 Temperature | 295 - 305 | °C | |
| Middle - Zone 2 Temperature | 280 - 295 | °C | |
| Rear - Zone 1 Temperature | 265 - 275 | °C | |
| Mold Temperature | 80 - 95 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 53 | MPa | ISO 527 |
| Tensile Strain, break | 32.3 | % | ISO 527 |
| Flexural Modulus, 2 mm/min | 2100 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min, 60°C | 800 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min, 100°C | 500 | MPa | ISO 178 |
| Flexural Stress, yield, 2 mm/min | 77 | MPa | ISO 178 |
| Flexural Stress, yield, 2 mm/min, 60°C | 32 | MPa | ISO 178 |
| Flexural Stress, yield, 2 mm/min, 100°C | 18 | MPa | ISO 178 |
| Flexural Strain, break, 2 mm/min | 7 | % | ISO 178 |
| Flexural Strain, break, 2 mm/min, 60°C | 7 | % | ISO 178 |
| Flexural Strain, break, 2 mm/min, 100°C | 7 | % | ISO 178 |
| Tensile Stress, yield | 56 | MPa | ASTM D638 |
| Tensile Stress, break | 55 | MPa | ASTM D638 |
| Tensile Strain, yield | 14 | % | ASTM D638 |
| Tensile Strain, break | 27 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2410 | MPa | ASTM D638 |
| Flexural Stress | 82 | MPa | ASTM D790 |
| Flexural Modulus | 2310 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 275°C/2.16 kg | 15 - 20 | cm³/10 min | ISO 1133 |
| Density | 1.03 | g/cm³ | ASTM D792 |
| Moisture Absorption, (23°C/50% RH/24 hrs) | 0.25 | % | ASTM D570 |
| Mold Shrinkage, flow, 24 hrs | 1.8 - 2.2 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 2.1 - 3.1 | % | ASTM D955 |
| Wear Factor Washer | 50 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified: Manual |
| Dynamic COF | 0.36 | - | ASTM D3702 Modified: Manual |
| Static COF | 0.27 | - | ASTM D3702 Modified: Manual |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 85 | °C | ISO 75/Af |
| CTE, 23°C to 60°C, flow | 7.70E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 60°C, xflow | 1.03E-04 | 1/°C | ISO 11359-2 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 77 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 7.74E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 1.03E-04 | 1/°C | ASTM E831 |
| Relative Temp Index, Elec | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 65 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 65 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.