PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
LNP STAT-KON EX99689C compound is based on Polyetherimide (PEI) resin containing 10% carbon fiber. Added features of this grade include: LNP Clean Compounding Technology, Electrically Conductive.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+06 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
UL Yellow Card Link | View | - | - |
UL Recognized, 94V-0 Flame Class Rating | 0.35 | mm | UL 94 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched, 23°C | 448 | J/m | ASTM D4812 |
Izod Impact, notched, 23°C | 53 | J/m | ASTM D256 |
Instrumented Dart Impact Energy @ peak, 23°C | 11 | J | ASTM D3763 |
Multiaxial Impact | 2 | J | ISO 6603 |
Izod Impact, unnotched 80*10*4 +23°C | 28 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 150 | °C | |
Drying Time | 4 - 6 | Hrs | |
Maximum Moisture Content | 0.02 | % | |
Melt Temperature | 360 - 400 | °C | |
Rear - Zone 1 Temperature | 360 - 380 | °C | |
Middle - Zone 2 Temperature | 370 - 390 | °C | |
Front - Zone 3 Temperature | 380 - 400 | °C | |
Nozzle Temperature | 390 - 400 | °C | |
Mold Temperature | 140 - 180 | °C | |
Back Pressure | 0.3 - 0.7 | MPa | |
Screw speed (Circumferential speed) | 0.2 - 0.3 | m/s | |
Vent Depth | 0.025 - 0.076 | mm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break | 161 | MPa | ASTM D638 |
Tensile Strain, break | 1.6 | % | ASTM D638 |
Tensile Modulus, 50 mm/min | 11650 | MPa | ASTM D638 |
Flexural Stress | 241 | MPa | ASTM D790 |
Flexural Modulus, 1.3 mm/min, 50 mm span | 8000 | MPa | ASTM D790 |
Tensile Stress, break | 137 | MPa | ISO 527 |
Tensile Strain, break | 1.2 | % | ISO 527 |
Tensile Modulus, 1 mm/min | 12630 | MPa | ISO 527 |
Flexural Stress | 216 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 7700 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Density | 1.31 | g/cm³ | ASTM D792 |
Moisture Absorption, (23°C/50% RH/24 hrs) | 0.3 | % | ASTM D570 |
Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D955 |
Mold Shrinkage, xflow, 24 hrs | 0.4 | % | ASTM D955 |
Mold Shrinkage, flow, 24 hrs | 0.17 | % | ISO 294 |
Mold Shrinkage, xflow, 24 hrs | 0.36 | % | ISO 294 |
Moisture Absorption (23°C / 50% RH) | 0.35 | % | ISO 62 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT, 1.82 MPa, 3.2mm, unannealed | 205 | °C | ASTM D648 |
CTE, -40°C to 40°C, flow | 3.29E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, xflow | 3.33E-05 | 1/°C | ASTM E831 |
CTE, -40°C to 40°C, flow | 3.30E-05 | 1/°C | ISO 11359-2 |
CTE, -40°C to 40°C, xflow | 3.33E-05 | 1/°C | ISO 11359-2 |
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 207 | °C | ISO 75/Af |
Relative Temp Index, Elec | 105 | °C | UL 746B |
Relative Temp Index, Mech w/impact | 105 | °C | UL 746B |
Relative Temp Index, Mech w/o impact | 105 | °C | UL 746B |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.