ELECTRICAL
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+03 | Ω | ASTM D257 |
LNP STAT-KON ZX05043 compound is based on Polyphenylene Ether / Polystyrene (PPE/PS) blend containing glass fiber, PTFE, carbon fiber. Added features of this grade include: Electrically Conductive, Internally Lubricated, Wear Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Surface Resistivity | 1.E+02 - 1.E+03 | Ω | ASTM D257 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Izod Impact, unnotched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1U |
Izod Impact, notched 80*10*4 +23°C | 5 | kJ/m² | ISO 180/1A |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Drying Temperature | 120 | °C | |
Drying Time | 4 | Hrs | |
Melt Temperature | 300 - 305 | °C | |
Front - Zone 3 Temperature | 300 - 310 | °C | |
Middle - Zone 2 Temperature | 290 - 300 | °C | |
Rear - Zone 1 Temperature | 275 - 290 | °C | |
Mold Temperature | 80 - 110 | °C | |
Back Pressure | 0.2 - 0.3 | MPa | |
Screw Speed | 30 - 60 | rpm |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Tensile Stress, break, 5 mm/min | 111 | MPa | ISO 527 |
Tensile Strain, break, 5 mm/min | 0.7 | % | ISO 527 |
Flexural Stress, break, 2 mm/min | 133 | MPa | ISO 178 |
Flexural Modulus, 2 mm/min | 12600 | MPa | ISO 178 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
Mold Shrinkage on Tensile Bar, flow | 0.5 - 1.5 | % | SABIC method |
Density | 1.41 | g/cm³ | ISO 1183 |
PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
---|---|---|---|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 130 | °C | ISO 75/Af |