LNP™ STAT-LOY™ Compound D3000IEU6

LNP STAT-LOY D3000IEU6 compound is based on Polycarbonate (PC) Copolymer that has been designed towards ATEX compliant applications requiring antistatic. The material has an optimized balance between surface resistivity and impact strength retention after hydro aging, and has excellent low temperature impact. The material is available in a wide range of dark and light colors, including UV stabilization.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding
Extrusion

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Aesthetics/Visual effects
Antistatic
Enhanced mold release
Good Processability
Heat Stabilized
High Flow
Hydrolytic Stability
Impact resistant
Low temperature impact
Thin Wall
Weatherable/UV stable

Industry

Material previously used in

Automotive Lighting
Commercial Appliance
Electrical
Electronic Components
Energy Management
Home Appliances
Material Handling
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Drone
Mobile Phone
Personal safety
Air Conditioning
ATM/Ticket Machine
Auto Electrical
Circuit Protection
Commercial Appliance
Conveyor
Displays
Document Handling
Enclosure/Housing/Cover
LED Lighting
Lighting
Medical Device
Non-LED Lighting
OLED
Personal Computing
Pharmaceutical Manufacturing
Pharmaceutical Packaging & Drug Delivery
Photovoltaic Components
Power Manangement
Semiconductor
Sensor
Vacuum Cleaner
Weaving Machine
inhaler
nebulizer
drug delivery
pill sorter
medical electrical connector
pipette tip

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Comparative Tracking Index	175	V	IEC 60112
Surface Resistivity, ROA	1.E+09 - 1.E+11	Ω	IEC 60093
Static Decay, 5000V to <50V	<0.01	Seconds	FTMS101B
Dielectric Constant
– at 60-90 GHz	2.73	-	-
Dissipation Factor
– at 60-90 GHz	0.022	-	-
Surface Resistivity	1.E+09 - 1.E+11	Ω	ASTM D257

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80104 +23°C*	60	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 +23°C*	65	kJ/m²	ISO 180/1A
*Izod Impact, notched 80104 -30°C*	60	kJ/m²	ISO 180/1A
*Izod Impact, notched 80103 -30°C*	65	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80103 +23°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	NB	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80103 -30°C*	NB	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	60	kJ/m²	ISO 179/1eA
*Charpy -30°C, V-notch Edgew 80104 sp=62mm*	60	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	NB	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	NB	kJ/m²	ISO 179/1eU
Multi-Axial Instrumented Impact Total Energy, 23°C	65	J	ISO 6603-2
Multi-Axial Instrumented Impact Energy @ peak, 23°C	55	J	ISO 6603-2
Multi-Axial Instrumented Impact Total Energy, -30°C	65	J	ISO 6603-2
Multi-Axial Instrumented Impact Energy @ peak, -30°C	55	J	ISO 6603-2
Izod Impact, notched, 23°C	850	J/m	ASTM D256
Izod Impact, notched, -30°C	750	J/m	ASTM D256
Izod Impact, unnotched, 23°C	NB	J/m	ASTM D4812
Izod Impact, unnotched, -30°C	NB	J/m	ASTM D4812
Instrumented Dart Impact Total Energy, 23°C	40	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, 23°C	35	J	ASTM D3763
Instrumented Dart Impact Peak Force, 23°C	4000	N	ASTM D3763
Instrumented Dart Impact Total Energy, -30°C	40	J	ASTM D3763
Instrumented Dart Impact Energy @ peak, -30°C	35	J	ASTM D3763
Instrumented Dart Impact Peak Force, -30°C	4800	N	ASTM D3763

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80 - 95	°C
Drying Time	2 - 4	Hrs
Drying Time (Cumulative)	8	Hrs
Maximum Moisture Content	0.03	%
Melt Temperature	240 - 260	°C
Rear - Zone 1 Temperature	220 - 240	°C
Middle - Zone 2 Temperature	230 - 250	°C
Front - Zone 3 Temperature	240 - 260	°C
Nozzle Temperature	240 - 260	°C
Mold Temperature	50 - 90	°C
Back Pressure	0.3 - 0.7	MPa
Screw speed (Circumferential speed)	0.15 - 0.2	m/s

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 1 mm/min	1750	MPa	ISO 527
Tensile Stress, yield, 50 mm/min	45	MPa	ISO 527
Tensile Strain, yield, 50 mm/min	5.5	%	ISO 527
Tensile Strain, break, 50 mm/min	>60	%	ISO 527
Tensile Nominal Strain, break, 50 mm/min	>60	%	ISO 527
Flexural Modulus, 2 mm/min	1825	MPa	ISO 178
Flexural Strength, 2 mm/min	70	MPa	ISO 178
Tensile Modulus, 50 mm/min	1750	MPa	ASTM D638
Tensile Stress, yld, Type I, 50 mm/min	45	MPa	ASTM D638
Tensile Strain, yld, Type I, 50 mm/min	5.5	%	ASTM D638
Tensile Strain, brk, Type I, 50 mm/min	>60	%	ASTM D638
Tensile Nominal Strain, brk, Type I, 50 mm/min	>60	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	1900	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	70	MPa	ASTM D790
Ball Indentation Hardness, H358/30	78	MPa	ISO 2039-1

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.16	g/cm³	ISO 1183
Moisture Absorption, (23°C/50% RH/24hrs)	0.15	%	ISO 62-4
Moisture Absorption, (23°C/50% RH/Equilibrium)	0.3	%	ISO 62-4
Water Absorption, (23°C/24hrs)	0.7	%	ISO 62-1
Water Absorption, (23°C/saturated)	3.5	%	ISO 62-1
Melt Volume Rate, MVR at 250°C/2.16 kg	5	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 250°C/5.0 kg	15	cm³/10 min	ISO 1133
Melt Volume Rate, MVR at 260°C/5.0 kg	23	cm³/10 min	ISO 1133
Specific Gravity	1.16	-	ASTM D792
Water Absorption, (23°C/24hrs)	0.7	%	ASTM D570
Water Absorption, (23°C/Saturated)	3.5	%	ASTM D570
Melt Flow Rate, 250°C/5.0 kgf	15	g/10 min	ASTM D1238
Mold Shrinkage, flow	0.5 - 0.7	%	SABIC method
Mold Shrinkage, xflow	0.6 - 0.8	%	SABIC method
Resistance to UV light
– Charpy impact (ISO 179) after Xenon-Arc weathering (ISO 4892-2)	PASS	-	IEC 60079-0

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	105	°C	ISO 75/Af
*HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm*	123	°C	ISO 75/Bf
Vicat Softening Temp, Rate B/50	123	°C	ISO 306
Vicat Softening Temp, Rate B/120	123	°C	ISO 306
Vicat Softening Temp, Rate A/50	137	°C	ISO 306
Vicat Softening Temp, Rate A/120	138	°C	ISO 306
CTE, 23°C to 50°C, flow	8.5E-05	1/°C	ISO 11359-2
CTE, 23°C to 50°C, xflow	1.1E-04	1/°C	ISO 11359-2
HDT, 1.82 MPa, 3.2mm, unannealed	105	°C	ASTM D648
HDT, 0.45 MPa, 3.2 mm, unannealed	123	°C	ASTM D648
Vicat Softening Temp, Rate B/50	123	°C	ASTM D1525
Vicat Softening Temp, Rate B/120	123	°C	ASTM D1525
CTE, 23°C to 50°C, flow	8.5E-05	1/°C	ASTM E831
CTE, 23°C to 50°C, xflow	1.1E-04	1/°C	ASTM E831
Ball Pressure Test, 125°C +/- 2°C	PASS	-	IEC 60695-10-2
Temperature Index (TI)
– Tensile Strength, 3.0 mm	108	°C	IEC 60216
– Tensile Strength, 1.5 mm	108	°C	IEC 60216

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES