LNP THERMOCOMP 6C004XXAR1 compound is based on Polycarbonate / Polybutylene Terephthalate (PC/PBT) resin containing 20% carbon fiber for Large Format Additive Manufacturing (LFAM) applications. Added features of this grade include: Improved Chemical Resistance, Lower Warp and Good Surface Finish.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Extruder L/D | 24 | - | |
| Drying Temperature | 110 | °C | |
| Drying Time | 4 | Hrs | |
| Drying Time (Cumulative) | 8 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Barrel - Zone 1 Temperature | 215 - 235 | °C | |
| Barrel - Zone 2 Temperature | 235 - 265 | °C | |
| Barrel - Zone 3 Temperature | 235 - 265 | °C | |
| Barrel - Zone 4 Temperature | 235 - 265 | °C | |
| Nozzle Temperature | 235 - 265 | °C | |
| Melt Temperature | 235 - 265 | °C | |
| Bed Temperature | 80 - 120 | °C | |
| Extruder Pressure | <11 | MPa |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, 5mm/min | |||
| – XZ Orientation | 106 | MPa | ASTM D638 Modified |
| – ZX Orientation | 106 | MPa | ASTM D638 Modified |
| Tensile Strain, 5mm/min | |||
| – XZ Orientation | 1.6 | % | ASTM D638 Modified |
| – ZX Orientation | 1.6 | % | ASTM D638 Modified |
| Tensile Stiffness, 5mm/min | |||
| – XZ Orientation | 10.6 | GPa | ASTM D638 Modified |
| – ZX Orientation | 10.6 | GPa | ASTM D638 Modified |
| Flexural Stress, 5mm/min | |||
| – XZ Orientation | 39 | MPa | ASTM D790 Modified |
| – ZX Orientation | 39 | MPa | ASTM D790 Modified |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.28 | - | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, annealed | 90 | °C | ASTM D648 |