LNP THERMOCOMP AC004XXAR1 compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing 20% carbon fiber for Large Format Additive Manufacturing (LFAM) applications. Added features of this grade include: Higher Stiffness vs. glass fiber, Easy Processing, Low warp and Good Print Surface quality, making them a good candidate material for a broad range of applications and tooling, including thermoforming and vacuum-forming.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Extruder L/D | 24 | - | |
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 - 0.1 | % | |
| Barrel - Zone 1 Temperature | 190 - 230 | °C | |
| Barrel - Zone 2 Temperature | 200 - 240 | °C | |
| Barrel - Zone 3 Temperature | 210 - 250 | °C | |
| Barrel - Zone 4 Temperature | 220 - 260 | °C | |
| Nozzle Temperature | 210 - 250 | °C | |
| Melt Temperature | 220 - 260 | °C | |
| Bed Temperature | 120 - 150 | °C | |
| Extruder Pressure | <13.5 | MPa |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, 5mm/min | |||
| – XZ Orientation | 89 | MPa | ASTM D638 Modified |
| – ZX Orientation | 18 | MPa | ASTM D638 Modified |
| Tensile Strain, 5mm/min | |||
| – XZ Orientation | 1 | % | ASTM D638 Modified |
| – ZX Orientation | 0.7 | % | ASTM D638 Modified |
| Tensile Stiffness, 5mm/min | |||
| – XZ Orientation | 11.8 | GPa | ASTM D638 Modified |
| – ZX Orientation | 2.9 | GPa | ASTM D638 Modified |
| Flexural Stress, 5mm/min | |||
| – XZ Orientation | 32 | MPa | ASTM D790 Modified |
| – ZX Orientation | 125 | MPa | ASTM D790 Modified |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.14 | - | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, annealed | 101 | °C | ASTM D648 |