LNP THERMOCOMP AM JC004XXAR1 is a compound based on PESU (Polyethersulfone) resin containing 20% carbon fiber for Large Format Additive manufacturing (LFAM) applications needing an inherent FR, reinforcement, and a high heat amorphous solution.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Extruder L/D | 24 | - | |
| Drying Temperature | 150 | °C | |
| Drying Time | 4 - 6 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Barrel - Zone 1 Temperature | 300 - 330 | °C | |
| Barrel - Zone 2 Temperature | 325 - 355 | °C | |
| Barrel - Zone 3 Temperature | 335 - 365 | °C | |
| Barrel - Zone 4 Temperature | 345 - 375 | °C | |
| Nozzle Temperature | 345 - 375 | °C | |
| Melt Temperature | 345 - 375 | °C | |
| Bed Temperature | 120 - 150 | °C | |
| Extruder Pressure | <17 | MPa |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, 5mm/min | |||
| – XZ Orientation | 84 | MPa | ASTM D638 Modified |
| – ZX Orientation | 23 | MPa | ASTM D638 Modified |
| Tensile Strain, 5mm/min | |||
| – XZ Orientation | 1.4 | % | ASTM D638 Modified |
| – ZX Orientation | 1.2 | % | ASTM D638 Modified |
| Tensile Stiffness, 5mm/min | |||
| – XZ Orientation | 7.8 | GPa | ASTM D638 Modified |
| – ZX Orientation | 2.2 | GPa | ASTM D638 Modified |
| Flexural Stress, 5mm/min | |||
| – XZ Orientation | 37 | MPa | ASTM D790 Modified |
| – ZX Orientation | 103 | MPa | ASTM D790 Modified |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.43 | - | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, annealed | 214 | °C | ASTM D648 |