LNP THERMOCOMP ZF004XXAR1 compound is based on Polyphenylene Ether / Polystyrene (PPE/PS) blend containing 20% glass fiber for Large Format Additive Manufacturing (LFAM) applications. Added features of this grade include: Lower Thermal Expansion, Improved Hydrolytic Stability, Higher Strength to Weight Ratio and Higher Temperature Performance vs. ABS.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Extruder L/D | 24 | - | |
| Drying Temperature | 120 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Barrel - Zone 1 Temperature | 270 - 305 | °C | |
| Barrel - Zone 2 Temperature | 280 - 320 | °C | |
| Barrel - Zone 3 Temperature | 280 - 320 | °C | |
| Barrel - Zone 4 Temperature | 280 - 320 | °C | |
| Nozzle Temperature | 280 - 320 | °C | |
| Melt Temperature | 270 - 305 | °C | |
| Bed Temperature | 100 - 120 | °C | |
| Extruder Pressure | <13.5 | MPa |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, 5mm/min | |||
| – XZ Orientation | 68 | MPa | ASTM D638 Modified |
| – ZX Orientation | 28 | MPa | ASTM D638 Modified |
| Tensile Strain, 5mm/min | |||
| – XZ Orientation | 2.0 | % | ASTM D638 Modified |
| – ZX Orientation | 1.9 | % | ASTM D638 Modified |
| Tensile Stiffness, 5mm/min | |||
| – XZ Orientation | 5.2 | GPa | ASTM D638 Modified |
| – ZX Orientation | 2.7 | GPa | ASTM D638 Modified |
| Flexural Stress, 5mm/min | |||
| – XZ Orientation | 51 | MPa | ASTM D790 Modified |
| – ZX Orientation | 103 | MPa | ASTM D790 Modified |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.22 | - | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, annealed | 131 | °C | ASTM D648 |