LNP THERMOCOMP AF006XXZ compound is based on Acrylonitrile Butadiene Styrene (ABS) resin containing 30% glass fiber.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 283 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 58 | J/m | ASTM D256 |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.05 - 0.1 | % | |
| Melt Temperature | 260 | °C | |
| Front - Zone 3 Temperature | 265 - 275 | °C | |
| Middle - Zone 2 Temperature | 230 - 245 | °C | |
| Rear - Zone 1 Temperature | 205 - 215 | °C | |
| Mold Temperature | 70 - 80 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 96 | MPa | ASTM D638 |
| Tensile Strain, break | 1.8 | % | ASTM D638 |
| Flexural Stress | 153 | MPa | ASTM D790 |
| Flexural modulus | 9170 | MPa | ASTM D790 |
| Tensile Stress, break | 83 | MPa | ISO 527 |
| Tensile Strain, break | 1.7 | % | ISO 527 |
| Flexural Stress | 119 | MPa | ISO 178 |
| Flexural Modulus | 8000 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ASTM D792 |
| Mold Shrinkage, flow, 24 hrs | 0.2 | % | ASTM D955 |
| Mold Shrinkage, xflow, 24 hrs | 0.4 | % | ASTM D955 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 102 | °C | ASTM D648 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 102 | °C | ISO 75/Af |
| Relative Temp Index, Elec | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 60 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 60 | °C | UL 746B |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 7 | kJ/m² | ISO 180/1A |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break, 5 mm/min | 82 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 1.4 | % | ISO 527 |
| Flexural Stress, break, 2 mm/min | 109 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6300 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.1 - 0.2 | % | SABIC method |
| Density | 1.26 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, 23°C to 60°C, flow | 2.3E-05 | 1/°C | ISO 11359-2 |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 102 | °C | ISO 75/Af |