LNP™ THERMOCOMP™ Compound DF002FVQ

LNP THERMOCOMP DF002FVQ compound is based on Polycarbonate (PC) resin containing 10% glass fiber and available in black color only. Added features of this grade include: Improved Plating Surface and Mechanical Performance targeted for Laser Direct Structuring (LDS) applications, Good Adhesion Strength, UL94 V0@0.8mm (black).

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Dielectrics
Electroplatable
High stiffness/Strength
Laser Direct Structuring

Industry

Material previously used in

Automotive Interiors
Electrical
Mobile Phone - Computer - Tablets
Personal Accessory

Applications

Possible usage of material

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant, 1.1 GHz	3.15	-	SABIC method
Dissipation Factor, 1.1 GHz	0.01	-	SABIC method
Dielectric Constant, 1.9 GHz	3.17	-	SABIC method
Dissipation Factor, 1.9 GHz	0.01	-	SABIC method
Dielectric Constant, 5 GHz	3.15	-	SABIC method
Dissipation Factor, 5 GHz	0.01	-	SABIC method
Dielectric Constant, 10 GHz	3.17	-	SABIC method
Dissipation Factor, 10 GHz	0.01	-	SABIC method
Dielectric Constant, 20 GHz	3.04	-	SABIC method
Dissipation Factor, 20 GHz	0.01	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	0.8	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	100	J/m	ASTM D256
Izod Impact, unnotched, 23°C	600	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	9	kJ/m²	ISO 180/1A
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	10	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	42	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110	°C
Drying Time	3 - 4	Hrs
Maximum Moisture Content	0.02	%
Melt Temperature	290 - 310	°C
Nozzle Temperature	285 - 310	°C
Front - Zone 3 Temperature	285 - 310	°C
Middle - Zone 2 Temperature	285 - 310	°C
Rear - Zone 1 Temperature	285 - 310	°C
Mold Temperature	100 - 130	°C
Back Pressure	0.1 - 0.3	MPa
Screw Speed	50 - 150	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	60	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	3	%	ASTM D638
Tensile Modulus, 5 mm/min	4610	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	4300	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	115	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	60	MPa	ISO 527
Tensile Strain, break, 5 mm/min	3.5	%	ISO 527
Tensile Modulus, 1 mm/min	4625	MPa	ISO 527
Flexural Modulus, 2 mm/min	4100	MPa	ISO 178
Flexural Strength, 2 mm/min	110	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.35	g/cm³	ASTM D792
Melt Flow Rate, 300°C/1.2 kgf	11	g/10 min	ASTM D1238
Mold Shrinkage, flow	0.2 - 0.4	%	SABIC method
Mold Shrinkage, xflow	0.3 - 0.5	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	126	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	120	°C	ASTM D648
CTE, -40°C to 40°C, flow	3.5E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	6.5E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	3.5E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	6.7E-05	1/°C	ISO 11359-2
Relative Temp Index, Elec	80	°C	UL 746B
Relative Temp Index, Mech w/impact	80	°C	UL 746B
Relative Temp Index, Mech w/o impact	80	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES