LNP™ THERMOCOMP™ Compound DF0061VI

LNP THERMOCOMP DF0061VI compound is based on Polycarbonate (PC) resin containing 30% glass fiber. Added features of this grade include: Improved Plating Surface and Mechanical Performance targeted for Laser Direct Structuring (LDS) applications, Non-Brominated, Non-Chlorinated Flame Retardant, Wide Processing Window.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polycarbonate (PC)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Dielectrics
Flame Retardant
High stiffness/Strength
Laser Direct Structuring
Non Cl/Br flame retardant

Industry

Material previously used in

Automotive Interiors
Electrical
Mobile Phone - Computer - Tablets
Personal Accessory

Applications

Possible usage of material

Electronic Components
Personal Computing
Wearables
Wireless Communications
mobile phone antenna
laptop antenna
wearable device antenna
lds
laser direct structuring
outdoor device antenna

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant
– 1.1 GHz	3.590	-	SABIC method
– 1.9 GHz	3.520	-	SABIC method
– 5 GHz	3.520	-	SABIC method
– 10 GHz	3.520	-	SABIC method
– 20 GHz	3.300	-	SABIC method
Dissipation Factor
– 1.1 GHz	0.009	-	SABIC method
– 1.9 GHz	0.008	-	SABIC method
– 5 GHz	0.008	-	SABIC method
– 10 GHz	0.008	-	SABIC method
– 20 GHz	0.008	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	0.6	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	70	J/m	ASTM D256
Izod Impact, unnotched, 23°C	400	J/m	ASTM D4812
*Izod Impact, notched 80104 +23°C*	7	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	30	kJ/m²	ISO 180/1U
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	7	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	30	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110 - 120	°C
Drying Time	3 - 4	Hrs
Melt Temperature	290 - 310	°C
Nozzle Temperature	285 - 310	°C
Front - Zone 3 Temperature	285 - 310	°C
Middle - Zone 2 Temperature	285 - 310	°C
Rear - Zone 1 Temperature	285 - 310	°C
Mold Temperature	100 - 130	°C
Back Pressure	0.1 - 0.3	MPa
Screw Speed	50 - 150	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	103	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	2	%	ASTM D638
Tensile Modulus, 5 mm/min	9400	MPa	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	8100	MPa	ASTM D790
Flexural Strength, 1.3 mm/min, 50 mm span	150	MPa	ASTM D790
Tensile Stress, break, 5 mm/min	106	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2	%	ISO 527
Tensile Modulus, 1 mm/min	9300	MPa	ISO 527
Flexural Modulus, 2 mm/min	8200	MPa	ISO 178
Flexural Strength, 2 mm/min	150	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Density	1.5	g/cm³	ASTM D792
Melt Flow Rate
– 300°C/1.2 kgf	13	g/10 min	ASTM D1238
– 300°C/2.16 kgf	25	g/10 min	ASTM D1238
Mold Shrinkage, flow	0.1 - 0.3	%	SABIC method
Mold Shrinkage, xflow	0.1 - 0.3	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	118	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	115	°C	ASTM D648
CTE, -40°C to 40°C, flow	2.2E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	6.0E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, flow	2.1E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	6.2E-05	1/°C	ISO 11359-2

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES