LNP THERMOCOMP DX13354X compound is based on Polycarbonate (PC) resin containing 30% glass fiber. Added features of this grade include: Improved Plating Surface and Mechanical Performance targeted for Laser Direct Structuring (LDS) applications, Improved Impact, Good Surface Aesthetics, Wide Processing Window and Colorable.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Dielectric Constant, 1.1 GHz | 3.47 | - | SABIC method |
| Dielectric Constant, 1.9 GHz | 3.45 | - | SABIC method |
| Dielectric Constant, 5 GHz | 3.45 | - | SABIC method |
| Dissipation Factor, 1.1 GHz | 0.013 | - | SABIC method |
| Dissipation Factor, 1.9 GHz | 0.012 | - | SABIC method |
| Dissipation Factor, 5 GHz | 0.011 | - | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 500 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 90 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 32 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m² | ISO 180/1A |
| Charpy Impact, unnotched, 23°C | 36 | kJ/m² | ISO 179/2C |
| Charpy Impact, notched, 23°C | 9 | kJ/m² | ISO 179/2C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 3 - 4 | Hrs | |
| Melt Temperature | 270 - 295 | °C | |
| Nozzle Temperature | 270 - 295 | °C | |
| Front - Zone 3 Temperature | 270 - 295 | °C | |
| Middle - Zone 2 Temperature | 270 - 295 | °C | |
| Rear - Zone 1 Temperature | 270 - 295 | °C | |
| Mold Temperature | 100 - 120 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 90 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 2.2 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 6900 | MPa | ASTM D638 |
| Flexural Strength, 1.3 mm/min, 50 mm span | 130 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 6300 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 90 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.1 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 6600 | MPa | ISO 527 |
| Flexural Strength, 2 mm/min | 130 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 6400 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.43 | - | ASTM D792 |
| Mold Shrinkage, flow, 3.2 mm | 0.1 - 0.3 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 0.3 - 0.5 | % | SABIC method |
| Melt Flow Rate, 280°C/2.16 kgf | 12 | g/10 min | ASTM D1238 |
| Melt Flow Rate, 300°C/1.2 kgf | 16 | g/10 min | ASTM D1238 |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 13 | cm³/10 min | ASTM D1238 |
| Density | 1.43 | g/cm³ | ISO 1183 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm | 124 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2 mm | 120 | °C | ASTM D648 |
| CTE, -40°C to 40°C, flow | 2.2E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, xflow | 6.3E-05 | 1/°C | ASTM E831 |
| CTE, -40°C to 40°C, flow | 1.9E-05 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 6.1E-05 | 1/°C | ISO 11359-2 |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 126 | °C | ISO 75/Bf |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 122 | °C | ISO 75/Af |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature