LNP THERMOCOMP IF006L compound is based on Nylon 6/12 resin containing 30% glass fiber. Added features of this grade include: Low Extractables.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | 1.5 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 587 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 85 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4 | Hrs | |
| Maximum Moisture Content | 0.12 - 0.2 | % | |
| Melt Temperature | 270 - 275 | °C | |
| Front - Zone 3 Temperature | 270 - 280 | °C | |
| Middle - Zone 2 Temperature | 260 - 270 | °C | |
| Rear - Zone 1 Temperature | 255 - 265 | °C | |
| Mold Temperature | 65 - 95 | °C | |
| Back Pressure | 0.2 - 0.3 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, break | 135 | MPa | ASTM D638 |
| Tensile Strain, break | 3 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 8750 | MPa | ASTM D638 |
| Flexural Stress | 206 | MPa | ASTM D790 |
| Flexural Modulus | 7790 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.31 | g/cm³ | ASTM D792 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 1.82 MPa, 3.2mm, unannealed | 198 | °C | ASTM D648 |