LNP™ THERMOCOMP™ Compound UF0067V

LNP THERMOCOMP UF0067V compound is based on Polyphthalamide (PPA) resin containing 30% glass fiber and available in black color only. Added features of this grade include: Improved Plating Surface and Mechanical Performance targeted for Laser Direct Structuring (LDS) applications, High Heat Resistance, SMT Process capable, Non-Brominated, Non-Chlorinated Flame Retardant.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyphthalamide (PPA)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Dielectrics
Flame Retardant
High stiffness/Strength
High temperature resistance
Laser Direct Structuring
No PFAS intentionally added
Non Cl/Br flame retardant

Industry

Material previously used in

Automotive Interiors
Electrical
Mobile Phone - Computer - Tablets
Personal Accessory

Applications

Possible usage of material

Antenna
mobile phone antenna
laptop antenna
lds
laser direct structuring
vcm
5g dipole antenna
dielectric
smt

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant, 1.1 GHz	3.560	-	SABIC method
Dissipation Factor, 1.1 GHz	0.009	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94V-0 Flame Class Rating	≥0.4	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	34	J/m	ASTM D256
Izod Impact, unnotched, 23°C	300	J/m	ASTM D4812

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	4 - 7	Hrs
Melt Temperature	290 - 330	°C
Nozzle Temperature	300 - 320	°C
Front - Zone 3 Temperature	300 - 320	°C
Middle - Zone 2 Temperature	280 - 300	°C
Rear - Zone 1 Temperature	260 - 280	°C
Mold Temperature	120 - 150	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Modulus, 5 mm/min	9500	MPa	ASTM D638
Tensile Stress, brk, Type I, 5 mm/min	104	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	1.6	%	ASTM D638
Flexural Modulus, 1.3 mm/min, 50 mm span	8500	MPa	ASTM D790
Flexural Stress, yld, 1.3 mm/min, 50 mm span	150	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.45	-	ASTM D792
Mold Shrinkage, flow	0.3	%	SABIC method
Mold Shrinkage, xflow	0.5	%	SABIC method
Water Absorption, (23°C/24hrs)	0.05	%	ISO 62-1

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm	276	°C	ASTM D648
HDT, 1.82 MPa, 3.2 mm	255	°C	ASTM D648
Relative Temp Index, Elec	65	°C	UL 746B
Relative Temp Index, Mech w/impact	65	°C	UL 746B
Relative Temp Index, Mech w/o impact	65	°C	UL 746B

Curve Data

view multipoint data represented visually on graphs.

You may click on the curve legends to select/unselect the curves.

Please login to view graphs, download multi-point data or literature

CAE Cards