LNP™ THERMOCOMP™ Compound WFC06IXP

LNP THERMOCOMP COMPOUND WFC06IXP is a compound based on Polybutylene terephthalate (PBT) containing Glass Fiber. Added features of this material include Chemical Resistance, Enhanced Dimensional Stability, Low Warpage, Dielectrics.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polybutylene Terephthalate (PBT)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Chemical Resistance
Dielectrics
Dimensional stability
Low Warpage
No PFAS intentionally added

Industry

Material previously used in

Automotive Interiors
Commercial Appliance
Electrical
Home Appliances

Applications

Possible usage of material

Automotive
Electrical
dielectric
adas cover
laser weldable
home appliance

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Constant
– 1.1 GHz	3.5	-	SABIC method
– 1.9 GHz	3.7	-	SABIC method
– 5 GHz	3.6	-	SABIC method
– 10 GHz	3.6	-	SABIC method
– 20 GHz	3.4	-	SABIC method
– 77 GHz	3.5	-	SABIC method
Dissipation Factor
– 1.1 GHz	0.008	-	SABIC method
– 1.9 GHz	0.008	-	SABIC method
– 5 GHz	0.007	-	SABIC method
– 10 GHz	0.007	-	SABIC method
– 20 GHz	0.008	-	SABIC method
– 77 GHz	0.009	-	SABIC method

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94HB Flame Class Rating	≥1.0	mm	UL 94

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, -20°C	120	J/m	ASTM D256
Izod Impact, notched, 23°C	160	J/m	ASTM D256
Izod Impact, unnotched, 23°C	1100	J/m	ASTM D4812
*Charpy 23°C, V-notch Edgew 80104 sp=62mm*	15	kJ/m²	ISO 179/1eA
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	65	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	120	°C
Drying Time	4	Hrs
Melt Temperature	260 - 290	°C
Nozzle Temperature	265 - 295	°C
Front - Zone 3 Temperature	260 - 290	°C
Middle - Zone 2 Temperature	260 - 290	°C
Rear - Zone 1 Temperature	250 - 280	°C
Mold Temperature	50 - 110	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	115	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	3	%	ASTM D638
Tensile Modulus, 5 mm/min	8370	MPa	ASTM D638
Flexural Strength, 1.3 mm/min, 50 mm span	190	MPa	ASTM D790
Flexural Modulus, 1.3 mm/min, 50 mm span	7660	MPa	ASTM D790

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	1.5	-	ASTM D792
Melt Volume Rate, MVR at 260°C/5.0 kg	11	cm³/10 min	ISO 1133
Mold Shrinkage, flow	0.2 - 0.4	%	SABIC method
Mold Shrinkage, xflow	0.4 - 0.6	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 3.2 mm, unannealed	218	°C	ASTM D648
HDT, 1.82 MPa, 3.2mm, unannealed	193	°C	ASTM D648
CTE
– 23°C to 80°C, flow	3.0E-05	1/°C	ASTM E831
– 23°C to 80°C, xflow	8.0E-05	1/°C	ASTM E831

Curve Data

view multipoint data represented visually on graphs.

You may click on the curve legends to select/unselect the curves.

Please login to view graphs, download multi-point data or literature

CAE Cards