LNP THERMOCOMP Z1C00VI compound is based on Polyphenylene Ether / Polystyrene (PPE/PS) blend containing proprietary fillers. Added features of this grade include: Ultra-Low Dielectric Constant and Loss Tangent for Laser Direct Structuring (LDS), High HDT, Low Warpage, Excellent Surface Finishing and Chemical Resistant.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Dielectric Constant, 1.1 GHz | 2.65 | - | SABIC method |
| Dielectric Constant, 1.9 GHz | 2.65 | - | SABIC method |
| Dielectric Constant, 10 GHz | 2.65 | - | SABIC method |
| Dissipation Factor, 1.1 GHz | 0.0012 | - | SABIC method |
| Dissipation Factor, 1.9 GHz | 0.0014 | - | SABIC method |
| Dissipation Factor, 10 GHz | 0.0020 | - | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 40 | J/m | ASTM D256 |
| Izod Impact, unnotched, 23°C | 600 | J/m | ASTM D4812 |
| Izod Impact, notched 80*10*4 +23°C | 6 | kJ/m² | ISO 180/1A |
| Izod Impact, unnotched 80*10*4 +23°C | 50 | kJ/m² | ISO 180/1U |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3 - 5 | Hrs | |
| Melt Temperature | 270 - 320 | °C | |
| Nozzle Temperature | 280 - 320 | °C | |
| Front - Zone 3 Temperature | 280 - 310 | °C | |
| Middle - Zone 2 Temperature | 270 - 300 | °C | |
| Rear - Zone 1 Temperature | 260 - 290 | °C | |
| Mold Temperature | 100 - 140 | °C | |
| Back Pressure | 10 | MPa | |
| Screw Speed | 100 | rpm |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yld, Type I, 50 mm/min | 70 | MPa | ASTM D638 |
| Tensile Stress, brk, Type I, 50 mm/min | 52 | MPa | ASTM D638 |
| Tensile Strain, yld, Type I, 50 mm/min | 4.5 | % | ASTM D638 |
| Tensile Strain, brk, Type I, 50 mm/min | 8 | % | ASTM D638 |
| Tensile Modulus, 50 mm/min | 2700 | MPa | ASTM D638 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 110 | MPa | ASTM D790 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 2700 | MPa | ASTM D790 |
| Tensile Stress, yield, 50 mm/min | 70 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 4.5 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 9 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2800 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 115 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2800 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Mold Shrinkage, flow | 0.5 - 0.7 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 155 | °C | ISO 75/Bf |