LNP™ VERTON™ Compound RVL36

LNP VERTON RVL36 is a compound based on Polyamide 66 (Nylon 66) resin containing 30% long glass fiber and 15% PTFE. Added features include Wear Resistant and Structural.

Product Family

LNP™ COMPOUNDS AND PC COPOLYMER RESINS

Polymer Family

Polyamide 66 (Nylon 66)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

High stiffness/Strength
Wear resistant

Industry

Material previously used in

Automotive Exteriors
Building Component
Commercial Appliance
Electrical
Home Appliances
Industrial General
Sport/Leisure

Applications

Possible usage of material

Electronic Components
Motorcycle

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, notched 80103 -40°C*	15	kJ/m²	ISO 180/1A
*Izod Impact, unnotched 80104 +23°C*	54	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -40°C*	50	kJ/m²	ISO 180/1U
*Izod Impact, notched 80104 +23°C*	16	kJ/m²	ISO 180/1A

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	80	°C
Drying Time	4	Hrs
Maximum Moisture Content	0.15 - 0.25	%
Melt Temperature	290 - 305	°C
Front - Zone 3 Temperature	290 - 300	°C
Middle - Zone 2 Temperature	290 - 300	°C
Rear - Zone 1 Temperature	280 - 295	°C
Mold Temperature	95 - 110	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, break, 5 mm/min	185	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2.9	%	ISO 527
Flexural Stress, yield, 2 mm/min	265	MPa	ISO 178
Flexural Strain, break, 2 mm/min	3.3	%	ISO 178
Flexural Modulus, 2 mm/min	8900	MPa	ISO 178
Flexural Strain, break, 2 mm/min, 60°C	3.9	%	ISO 178
Flexural Strain, break, 2 mm/min, 100°C	4	%	ISO 178
Flexural Strain, break, 2 mm/min, 150°C	3.6	%	ISO 178
Flexural Strain, break, 2 mm/min, 200°C	3.4	%	ISO 178
Flexural Stress, yield, 2 mm/min, 60°C	208	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 100°C	155	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 150°C	129	MPa	ISO 178
Flexural Stress, yield, 2 mm/min, 200°C	105	MPa	ISO 178
Flexural Modulus, 2 mm/min, 60°C	7100	MPa	ISO 178
Flexural Modulus, 2 mm/min, 100°C	5800	MPa	ISO 178
Flexural Modulus, 2 mm/min, 150°C	5200	MPa	ISO 178
Flexural Modulus, 2 mm/min, 200°C	4800	MPa	ISO 178

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Mold Shrinkage, flow, 24 hrs	0.25	%	ISO 294
Mold Shrinkage, xflow, 24 hrs	0.69	%	ISO 294
Wear Factor Washer	12	10^-10 in^5-min/ft-lb-hr	ASTM D3702 Modified: Manual
Density	1.53	g/cm³	ISO 1183
Water Absorption, (23°C/24hrs)	1.37	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.4	%	ISO 62

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Heat	1846	J/kg-K	ASTM E1269
*HDT/Af, 1.8 MPa Flatw 80104 sp=64mm*	258	°C	ISO 75/Af
Thermal Conductivity	0.25	W/m-K	ASTM D5930

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES