NORYL™ Resin SE1GFN3E

NORYL SE1GFN3E resin is a 30% glass fiber reinforced blend of polyphenylene ether (PPE) + polystyrene (PS). This injection moldable grade contains non-brominated, non-chlorinated flame retardant and carries a UL94 flame rating of V1 at 1.5mm and RTI of 110C. NORYL SE1GFN3E exhibits high heat resistance, good dielectric strength, dimensional stability, hydrolytic stability, and very low moisture absorption. This material is an excellent candidate for a variety of applications such as solar frames, unattended power supply (UPS) inverter/charger, indoor and outdoor electrical enclosures / housings / connectors, and wall plates / sockets / switches.

Product Family

NORYL™ RESINS

Polymer Family

Polyphenylene Ether + PS (PPE+PS)

Processing Technology

Injection Molding

Where to buy

You can get in touch with us in these regions to buy the material

Colors

All colors are customizable. Refer our ColorXpress tool to check color availability

+more

Features

Key characteristics of the material

Amorphous
Dimensional stability
Flame Retardant
High stiffness/Strength
Hydrolytic Stability
Low Moisture Absorption
Low Shrinkage
Low Specific Gravity
Low Warpage
No PFAS intentionally added
Non Cl/Br flame retardant
Non halogenated flame retardant

Industry

Material previously used in

Electrical
Energy Management
Mobile Phone - Computer - Tablets

Applications

Possible usage of material

Building and Construction
Building Accessory
Circuit Protection
Cladding/Roof
Document Handling
Electrical
Electronic Components
Electronic Material Handling
Enclosure/Housing/Cover
Enclosures
Energy Management
Fixture Bath/Shower
Furnace/Heater
Hot Water System
Inverter
Lawn/Garden
LED Lighting
Medical Device
Motorcycle
Personal Care
Pump
Refrigerator
Renal and Blood Handling
Security/Detection
Small Appliance
Surgical Devices
Washing Machine
Wireless Communications
Wiring Devices
fuse box
connector
junction box
power
energy
solar
pv
micro inverter
alternative energy
electrical component
electronic component
battery protection

Technical Datasheet Data

View different characteristics of the material at a standard test conditions

Region

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Strength, in oil, 3.2 mm	-	kV/mm	ASTM D149
Relative Permittivity, 50/60 Hz	-	-	ASTM D150
Dissipation Factor, 50/60 Hz	-	-	ASTM D150
High Voltage Arc Track Rate {PLC}	-	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	-	PLC Code	UL 746A
High Amp Arc Ignition (HAI), PLC 2	-	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 0	-	mm	UL 746A
Arc Resistance, Tungsten {PLC}	-	PLC Code	ASTM D495

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	-	-	-
UL Recognized, 94V-0 Flame Class Rating	-	mm	UL 94
UL Recognized, 94V-1 Flame Class Rating	-	mm	UL 94
Oxygen Index (LOI)	-	%	ASTM D2863

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	-	J/m	ASTM D256
Izod Impact, notched, -40°C	-	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	-	°C
Drying Time	-	Hrs
Drying Time (Cumulative)	-	Hrs
Maximum Moisture Content	-	%
Melt Temperature	-	°C
Nozzle Temperature	-	°C
Front - Zone 3 Temperature	-	°C
Middle - Zone 2 Temperature	-	°C
Rear - Zone 1 Temperature	-	°C
Mold Temperature	-	°C
Back Pressure	-	MPa
Screw Speed	-	rpm
Shot to Cylinder Size	-	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	-	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	-	%	ASTM D638
Flexural Stress, yld, 2.6 mm/min, 100 mm span	-	MPa	ASTM D790
Flexural Modulus, 2.6 mm/min, 100 mm span	-	MPa	ASTM D790
Hardness, Rockwell L	-	-	ASTM D785

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	-	-	ASTM D792
Water Absorption, (23°C/24hrs)	-	%	ASTM D570
Mold Shrinkage, flow, 3.2 mm	-	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 6.4 mm, unannealed	-	°C	ASTM D648
HDT, 1.82 MPa, 6.4 mm, unannealed	-	°C	ASTM D648
CTE, -40°C to 95°C, flow	-	1/°C	ASTM E831
Relative Temp Index, Elec	-	°C	UL 746B
Relative Temp Index, Mech w/impact	-	°C	UL 746B
Relative Temp Index, Mech w/o impact	-	°C	UL 746B

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Dielectric Strength, in oil, 3.2 mm	-	kV/mm	ASTM D149
Relative Permittivity, 50/60 Hz	-	-	ASTM D150
Dissipation Factor, 50/60 Hz	-	-	ASTM D150
High Voltage Arc Track Rate {PLC}	-	PLC Code	UL 746A
Comparative Tracking Index (UL) {PLC}	-	PLC Code	UL 746A
High Amp Arc Ignition (HAI), PLC 2	-	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 0	-	mm	UL 746A

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	-	-	-
UL Yellow Card Link 2	-	-	-
UL Recognized, 94V-1 Flame Class Rating	-	mm	UL 94
Oxygen Index (LOI)	-	%	ASTM D2863

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Izod Impact, notched, 23°C	-	J/m	ASTM D256
Izod Impact, notched, -40°C	-	J/m	ASTM D256

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	-	°C
Drying Time	-	Hrs
Drying Time (Cumulative)	-	Hrs
Maximum Moisture Content	-	%
Melt Temperature	-	°C
Nozzle Temperature	-	°C
Front - Zone 3 Temperature	-	°C
Middle - Zone 2 Temperature	-	°C
Rear - Zone 1 Temperature	-	°C
Mold Temperature	-	°C
Back Pressure	-	MPa
Screw Speed	-	rpm
Shot to Cylinder Size	-	%

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Tensile Stress, brk, Type I, 5 mm/min	-	MPa	ASTM D638
Tensile Strain, brk, Type I, 5 mm/min	-	%	ASTM D638
Flexural Stress, yld, 2.6 mm/min, 100 mm span	-	MPa	ASTM D790
Flexural Modulus, 2.6 mm/min, 100 mm span	-	MPa	ASTM D790
Hardness, Rockwell L	-	-	ASTM D785

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Specific Gravity	-	-	ASTM D792
Water Absorption, (23°C/24hrs)	-	%	ASTM D570
Mold Shrinkage, flow, 3.2 mm	-	%	SABIC method

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
HDT, 0.45 MPa, 6.4 mm, unannealed	-	°C	ASTM D648
HDT, 1.82 MPa, 6.4 mm, unannealed	-	°C	ASTM D648
CTE, -40°C to 95°C, flow	-	1/°C	ASTM E831
Relative Temp Index, Elec	-	°C	UL 746B
Relative Temp Index, Mech w/impact	-	°C	UL 746B
Relative Temp Index, Mech w/o impact	-	°C	UL 746B

ELECTRICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Volume Resistivity	1.E+15	Ω.cm	IEC 60093
Surface Resistivity, ROA	>1.E+15	Ω	IEC 60093
Dielectric Strength, in oil, 0.8 mm	30	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 1.6 mm	25	kV/mm	IEC 60243-1
Dielectric Strength, in oil, 3.2 mm	16	kV/mm	IEC 60243-1
Relative Permittivity, 1 MHz	3	-	IEC 60250
Dissipation Factor, 50/60 Hz	0.008	-	IEC 60250
Dissipation Factor, 1 MHz	0.005	-	IEC 60250
Comparative Tracking Index	300	V	IEC 60112
Relative Permittivity, 50/60 Hz	3.1	-	IEC 60250
Comparative Tracking Index (UL) {PLC}	3	PLC Code	UL 746A
High Voltage Arc Track Rate {PLC}	4	PLC Code	UL 746A
High Amp Arc Ignition (HAI), PLC 3	≥6	mm	UL 746A
High Amp Arc Ignition (HAI), PLC 4	≥1.5	mm	UL 746A
Hot-Wire Ignition (HWI), PLC 0	≥1.5	mm	UL 746A

FLAME CHARACTERISTICS

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
UL Yellow Card Link	View	-	-
UL Recognized, 94-5VA Flame Class Rating	≥3	mm	UL 94
UL Recognized, 94V-0 Flame Class Rating	≥6	mm	UL 94
UL Recognized, 94V-1 Flame Class Rating	≥1.5	mm	UL 94
Glow Wire Flammability Index 960°C, passes at	3.2	mm	IEC 60695-2-12
UV-light, water exposure/immersion	F2	-	UL 746C
Oxygen Index (LOI)	31	%	ISO 4589

IMPACT

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
*Izod Impact, unnotched 80104 +23°C*	25	kJ/m²	ISO 180/1U
*Izod Impact, unnotched 80104 -30°C*	25	kJ/m²	ISO 180/1U
*Charpy 23°C, Unnotch Edgew 80104 sp=62mm*	30	kJ/m²	ISO 179/1eU
*Charpy -30°C, Unnotch Edgew 80104 sp=62mm*	30	kJ/m²	ISO 179/1eU

INJECTION MOLDING

PROPERTIES	TYPICAL VALUES	UNITS
Drying Temperature	110 - 120	°C
Drying Time	2 - 3	Hrs
Melt Temperature	300 - 320	°C
Nozzle Temperature	280 - 300	°C
Front - Zone 3 Temperature	300 - 320	°C
Middle - Zone 2 Temperature	280 - 300	°C
Rear - Zone 1 Temperature	260 - 280	°C
Hopper Temperature	80 - 100	°C
Mold Temperature	100 - 130	°C

MECHANICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Taber Abrasion, CS-17, 1 kg	55	mg/1000cy	SABIC method
Tensile Stress, break, 5 mm/min	105	MPa	ISO 527
Tensile Strain, break, 5 mm/min	2	%	ISO 527
Tensile Modulus, 1 mm/min	8000	MPa	ISO 527
Flexural Stress, break, 2 mm/min	130	MPa	ISO 178
Flexural Modulus, 2 mm/min	6000	MPa	ISO 178
Ball Indentation Hardness, H358/30	130	MPa	ISO 2039-1

PHYSICAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
Mold Shrinkage on Tensile Bar, flow	0.1 - 0.3	%	SABIC method
Density	1.29	g/cm³	ISO 1183
Water Absorption, (23°C/saturated)	0.23	%	ISO 62-1
Moisture Absorption (23°C / 50% RH)	0.07	%	ISO 62
Melt Volume Rate, MVR at 280°C/10.0 kg	9	cm³/10 min	ISO 1133

THERMAL

PROPERTIES	TYPICAL VALUES	UNITS	TEST METHODS
CTE, -40°C to 40°C, flow	3.7E-05	1/°C	ASTM E831
CTE, -40°C to 40°C, xflow	5.5E-05	1/°C	ASTM E831
Thermal Conductivity	0.28	W/m-°C	ISO 8302
CTE, -40°C to 40°C, flow	3.7E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	5.5E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, flow	3.E-05	1/°C	ISO 11359-2
CTE, 23°C to 80°C, xflow	7.E-05	1/°C	ISO 11359-2
Ball Pressure Test, 125°C +/- 2°C	PASSES	-	IEC 60695-10-2
Ball Pressure Test, approximate maximum	140	°C	IEC 60695-10-2
Vicat Softening Temp, Rate A/50	155	°C	ISO 306
Vicat Softening Temp, Rate B/50	145	°C	ISO 306
Vicat Softening Temp, Rate B/120	150	°C	ISO 306
*HDT/Be, 0.45MPa Edgew 120104 sp=100mm*	140	°C	ISO 75/Be
*HDT/Ae, 1.8 MPa Edgew 120104 sp=100mm*	135	°C	ISO 75/Ae
Relative Temp Index, Elec	110	°C	UL 746B
Relative Temp Index, Mech w/impact	105	°C	UL 746B
Relative Temp Index, Mech w/o impact	110	°C	UL 746B

Register for High value Multi-Point Data

Access validated product data to streamline material selection
Get inspired by innovative application ideas
Register for high value multi-point data and a personalized experience

THIS SITE USES COOKIES

NORYL™ Resin SE1GFN3E

Product Family

Polymer Family

Processing Technology

Where to buy

Colors

Features

Industry

Applications

Technical Datasheet Data

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL

ELECTRICAL

FLAME CHARACTERISTICS

IMPACT

INJECTION MOLDING

MECHANICAL

PHYSICAL

THERMAL