NORYL SE90 is an unfilled, flame retardant material with a Vicat B/120 of 110?C according ISO 306. NORYL SE90 is V1 at 1.6 mm according UL94 and halogen free according VDE/DIN 472 part 815.
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Surface Resistivity | 1.E+16 | Ω | ASTM D257 |
| Relative Permittivity, 50/60 Hz | 2.69 | - | ASTM D150 |
| Arc Resistance, Tungsten {PLC} | 7 | PLC Code | ASTM D495 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Recognized, 94V-1 Flame Class Rating | 1.5 | mm | UL 94 |
| UL Recognized, 94-5VA Flame Class Rating | 3 | mm | UL 94 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched, 23°C | 274 | J/m | ASTM D256 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, yield | 39 | MPa | SABIC - Japan Method |
| Tensile Strain, break | 55 | % | SABIC - Japan Method |
| Flexural Stress | 64 | MPa | ASTM D790 |
| Flexural Modulus | 2200 | MPa | ASTM D790 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Specific Gravity | 1.1 | - | ASTM D792 |
| Water Absorption, (23°C/24hrs) | 0.07 | % | ASTM D570 |
| Mold Shrinkage, flow, 3.2 mm | 0.5 - 0.7 | % | SABIC method |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| HDT, 0.45 MPa, 3.2 mm, unannealed | 90 | °C | ASTM D648 |
| CTE, -30°C to 30°C | 7.00E-05 | 1/°C | TMA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Volume Resistivity | 1.E+15 | Ω.cm | IEC 60093 |
| Surface Resistivity, ROA | >1.E+15 | Ω | IEC 60093 |
| Dielectric Strength, in oil, 0.8 mm | 33 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 1.6 mm | 26 | kV/mm | IEC 60243-1 |
| Dielectric Strength, in oil, 3.2 mm | 16 | kV/mm | IEC 60243-1 |
| Relative Permittivity, 1 MHz | 2.7 | - | IEC 60250 |
| Dissipation Factor, 50/60 Hz | 0.009 | - | IEC 60250 |
| Dissipation Factor, 1 MHz | 0.006 | - | IEC 60250 |
| Comparative Tracking Index | 200 | V | IEC 60112 |
| Relative Permittivity, 50/60 Hz | 2.8 | - | IEC 60250 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Recognized, 94V-1 Flame Class Rating | 1.5 | mm | UL 94 |
| Glow Wire Flammability Index 960°C, passes at | 3.2 | mm | IEC 60695-2-12 |
| Oxygen Index (LOI) | 30 | % | ISO 4589 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, notched 80*10*4 +23°C | 20 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 9 | kJ/m² | ISO 180/1A |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 20 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 10 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 80 - 100 | °C | |
| Drying Time | 2 - 3 | Hrs | |
| Melt Temperature | 260 - 280 | °C | |
| Nozzle Temperature | 240 - 260 | °C | |
| Front - Zone 3 Temperature | 260 - 280 | °C | |
| Middle - Zone 2 Temperature | 240 - 260 | °C | |
| Rear - Zone 1 Temperature | 220 - 240 | °C | |
| Hopper Temperature | 60 - 80 | °C | |
| Mold Temperature | 60 - 80 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Taber Abrasion, CS-17, 1 kg | 50 | mg/1000cy | SABIC method |
| Tensile Stress, yield, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Stress, break, 50 mm/min | 45 | MPa | ISO 527 |
| Tensile Strain, yield, 50 mm/min | 3 | % | ISO 527 |
| Tensile Strain, break, 50 mm/min | 30 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 2400 | MPa | ISO 527 |
| Flexural Stress, yield, 2 mm/min | 75 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 2300 | MPa | ISO 178 |
| Ball Indentation Hardness, H358/30 | 87 | MPa | ISO 2039-1 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage on Tensile Bar, flow | 0.5 - 0.7 | % | SABIC method |
| Density | 1.1 | g/cm³ | ISO 1183 |
| Water Absorption, (23°C/saturated) | 0.43 | % | ISO 62-1 |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Melt Volume Rate, MVR at 280°C/3.8 kg | 16 | cm³/10 min | ISO 1133 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Thermal Conductivity | 0.24 | W/m-°C | ISO 8302 |
| CTE, 23°C to 80°C, flow | 7.E-05 | 1/°C | ISO 11359-2 |
| CTE, 23°C to 80°C, xflow | 9.E-05 | 1/°C | ISO 11359-2 |
| Ball Pressure Test, 75°C +/- 2°C | PASSES | - | IEC 60695-10-2 |
| Ball Pressure Test, approximate maximum | 100 | °C | IEC 60695-10-2 |
| Vicat Softening Temp, Rate A/50 | 110 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 105 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 110 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 95 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 85 | °C | ISO 75/Ae |
| Relative Temp Index, Elec | 95 | °C | UL 746B |
| Relative Temp Index, Mech w/impact | 75 | °C | UL 746B |
| Relative Temp Index, Mech w/o impact | 95 | °C | UL 746B |