NORYL WM330G resin is a 30% glass fiber reinforced blend of impact modified polyphenylene ether (PPE) + polystyrene (PS). This injection moldable material is FC EU, FDA food contact compliant*, NSF/ANSI 61, ACS, WRAS and KTW-WBGL listing** for global potable water use for specific colors is available. NORYL WM330G resin exhibits good fatigue performance, excellent long-term hydrolytic stability, very low moisture absorption, heat / hot water resistance and is an excellent candidate for a variety of water management applications such as pump housings, impellers, shower/faucet, membrane housings and valves.
*Restrictions may apply in the case of applications involving fatty foods. Please review the food contact declaration for details.
** Potable water listing is color dependent
All colors are customizable. Refer our ColorXpress tool to check color availability
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| UL Yellow Card Link | View | - | - |
| UL Recognized, 94HB Flame Class Rating | ≥1.5 | mm | UL 94 |
| Glow Wire Ignitability Temperature, 1.5 mm | 825 | °C | IEC 60695-2-13 |
| Glow Wire Ignitability Temperature, 3.0 mm | 800 | °C | IEC 60695-2-13 |
| Glow Wire Flammability Index, 1.5 mm | 825 | °C | IEC 60695-2-12 |
| Glow Wire Flammability Index, 3.0 mm | 775 | °C | IEC 60695-2-12 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Izod Impact, unnotched, 23°C | 520 | J/m | ASTM D4812 |
| Izod Impact, unnotched, -30°C | 550 | J/m | ASTM D4812 |
| Izod Impact, notched, 23°C | 105 | J/m | ASTM D256 |
| Izod Impact, notched, -30°C | 85 | J/m | ASTM D256 |
| Izod Impact, unnotched 80*10*4 +23°C | 42 | kJ/m² | ISO 180/1U |
| Izod Impact, unnotched 80*10*4 -30°C | 45 | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 12 | kJ/m² | ISO 180/1A |
| Izod Impact, notched 80*10*4 -30°C | 9 | kJ/m² | ISO 180/1A |
| Charpy 23°C, Unnotch Edgew 80*10*4 sp=62mm | 45 | kJ/m² | ISO 179/1eU |
| Charpy -30°C, Unnotch Edgew 80*10*4 sp=62mm | 50 | kJ/m² | ISO 179/1eU |
| Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm | 12 | kJ/m² | ISO 179/1eA |
| Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm | 9 | kJ/m² | ISO 179/1eA |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 2 - 4 | Hrs | |
| Maximum Moisture Content | 0.02 | % | |
| Melt Temperature | 290 - 330 | °C | |
| Nozzle Temperature | 290 - 320 | °C | |
| Front - Zone 3 Temperature | 300 - 310 | °C | |
| Middle - Zone 2 Temperature | 280 - 300 | °C | |
| Rear - Zone 1 Temperature | 270 - 280 | °C | |
| Hopper Temperature | 60 - 80 | °C | |
| Mold Temperature | 80 - 120 | °C |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Tensile Stress, brk, Type I, 5 mm/min | 131 | MPa | ASTM D638 |
| Tensile Strain, brk, Type I, 5 mm/min | 3.0 | % | ASTM D638 |
| Tensile Modulus, 5 mm/min | 9425 | MPa | ASTM D638 |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 7650 | MPa | ASTM D790 |
| Flexural Stress, brk, 1.3 mm/min, 50 mm span | 188 | MPa | ASTM D790 |
| Tensile Stress, break, 5 mm/min | 131 | MPa | ISO 527 |
| Tensile Strain, break, 5 mm/min | 2.4 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 9475 | MPa | ISO 527 |
| Flexural Stress, break, 2 mm/min | 200 | MPa | ISO 178 |
| Flexural Modulus, 2 mm/min | 8440 | MPa | ISO 178 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| Mold Shrinkage, flow, 3.2 mm | 0.1 - 0.3 | % | SABIC method |
| Mold Shrinkage, xflow, 3.2 mm | 0.2 - 0.5 | % | SABIC method |
| Moisture Absorption (23°C / 50% RH) | 0.06 | % | ISO 62 |
| Water Absorption, (23°C/saturated) | 0.2 | % | ISO 62-1 |
| Density | 1.3 | g/cm³ | ISO 1183 |
| Melt Volume Rate, MVR at 300°C/10.0 kg | 26 | cm³/10 min | ISO 1133 |
| Melt Flow Rate, 300°C/10 kgf | 30 | g/10 min | ASTM D1238 |
| PROPERTIES | TYPICAL VALUES | UNITS | TEST METHODS |
|---|---|---|---|
| CTE, -40°C to 40°C, flow | 1.8E-5 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 5.5E-5 | 1/°C | ISO 11359-2 |
| Vicat Softening Temp, Rate A/50 | 164 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/50 | 154 | °C | ISO 306 |
| Vicat Softening Temp, Rate A/120 | 167 | °C | ISO 306 |
| Vicat Softening Temp, Rate B/120 | 156 | °C | ISO 306 |
| HDT/Be, 0.45MPa Edgew 120*10*4 sp=100mm | 155 | °C | ISO 75/Be |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 149 | °C | ISO 75/Ae |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 153 | °C | ASTM D648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 147 | °C | ASTM D648 |
view multipoint data represented visually on graphs.
You may click on the curve legends to select/unselect the curves.
Please login to view graphs, download multi-point data or literature
Please login to view graphs, download multi-point data or literature
Your PDF is downloading. Please wait.